以铝粉为主要填料,聚氨酯为粘合剂,制备了8～14μm波段发射率低至0.10的低红外发射率涂层.研究了基板处理、涂层厚度和固化温度对涂层力学性能的影响,并对其在涂料中的作用机理进行了探讨.结果表明,当基板用偶联剂处理、涂层厚度为30μm、热处理温度为80℃时,制得的涂层能在保持低红外发射率的同时具有最佳的力学性能.
参考文献
| [1] | Chen J;Zhou YM;Nan QL;Sun YQ;Ye XY;Wang ZQ .Synthesis, characterization and infrared emissivity study of polyurethane/TiO2 nanocomposites[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(23):9154-9158. |
| [2] | Zueco, J;Alhama, F .Inverse estimation of temperature dependent emissivity of solid metals[J].Journal of Quantitative Spectroscopy & Radiative Transfer,2006(1):73-86. |
| [3] | 游毓聪,杜仕国,施冬梅,纪占敏,张彬.红外隐身涂料黏合剂的应用与研究[J].现代涂料与涂装,2006(07):50-51,54. |
| [4] | Lin Baoping;Liu Hongjian et al.Structure and infrared emissivity of silicon-containing polyimide/BaTiO3 nsnocomposite films[J].Journal of Solid State Chemistry,2004,177(10):3849. |
| [5] | 刘永峙,韩爱军,李校远.红外隐身材料的研究现状与发展方向[J].材料导报,2004(z1):216-218. |
| [6] | Yu Huijuan;Xu Guoyue et al.Low infrared emissivity of polyurethane/Cu composite coatings[J].Applied Surface Science,2009,255:6077. |
| [7] | 余慧娟,徐国跃,沈轩,邵春明.8～14 μm波段低发射率涂料的制备与优化研究[J].兵器材料科学与工程,2008(06):49-52. |
| [8] | 陈广祥,李金玲,叶代勇.HDI三聚体改性水性聚氨酯复合分散体的研究[J].涂料工业,2009(10):41-45. |
| [9] | 周学梅,张焰.硅烷偶联剂在涂装前处理中的应用[J].表面技术,2005(01):66-67,72. |
| [10] | 乔红斌,佘金阳,古绪鹏,杨建国.硅烷偶联剂在涂料与涂装中的应用进展[J].安徽工业大学学报（自然科学版）,2008(04):379-382. |
| [11] | 袁立新,狄志刚,傅敏,朱晓丰,许后麟,许昀.常温固化耐高温环氧改性有机硅聚氨酯防腐蚀涂料的研制[J].上海涂料,2005(11):9-12. |
| [12] | 鄢建辉,汪久根,綦振慧.单层涂层最佳厚度的有限元分析[J].机械设计,2004(01):7-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%