采用SEM、TEM和化学相分析等手段研究了一种新型Ni-Cr-Mo高强耐蚀合金中碳化物的热稳定性,结果表明:标准热处理态下的新合金由大小不均匀的等轴晶组成,其中的碳化物主要为聚集分布的颗粒状Mo6C.在600℃时效时,Mo6C相的形态、尺寸和数量均无明显变化,这表明它在该温度下具有较好的热稳定性.但在650℃时效时,随着时效时间的延长,Mo6C相的形态将逐渐由颗粒状向片状转变,当时效时间超过500 h后,它将逐渐溶解,与此同时条状的Cr23C6相将在合金晶界逐渐析出.这表明Mo6C相在该温度下是不稳定的,故新合金的使用温度应低于650℃.
参考文献
| [1] | Agarwal D C;Herda W R .[J].Materials and Corrosion,1997,48:542. |
| [2] | Dymek S;Wrobel M;Stepniowska E et al.[J].Materials Characterization,2010,61:769. |
| [3] | Basuki W W;Kraft O;Aktaa J .[J].Materials Science and Engineering A,2012,538:340. |
| [4] | Zhang Q;Tang R;Yin K J et al.[J].Corrosion Science,2009,51:2092. |
| [5] | Pike L M;Klarstrom D L.Corrosion 2004[M].Houston:NACE International,2004:239. |
| [6] | Dymek S;Dollar M;Farooqi M .[J].Materials Science and Engineering A,2001,319-321:284. |
| [7] | Akhter J I;Shaikh M A;Ahmad M et al.[J].Journal of Materials Science Letters,2001,20:333. |
| [8] | Tawancy H M .[J].Journal of Materials Science,1981,16:2883. |
| [9] | Lu Y L;Pike L M;Brooks C R et al.[J].Scripta Materialia,2007,56:121. |
| [10] | Raghavan M;Berkowitz B J;Scanlon J C .[J].Metallurgical Transactions A,1982,13:979. |
| [11] | Kumar M;Vasudevan V K .[J].ACTA MATERIALIA,1996,44(12):4865. |
| [12] | Li X B;Xie Y Q;Zhu Y X .[J].Materials and Corrosion,2005,56(09):636. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%