基于密度泛函理论,采用总能量计算方法与结合超软赝势平面波函数方法,对LaNi4.5Mn0.5储氢合金及其氢化物的晶体几何结构进行了优化,计算了其相应的总体能量、晶体结构、能带结构、及态密度分布等,从理论上给出了其结构参数及性质.结果表明,锰取代3g位后合金晶胞略有膨胀,并伴随着晶体稳定性变差.LaNi4.5Mn0.5合金中EF附近的态密度贡献最主要来自La的p电子,以及Ni和Mn原子的d电子.
参考文献
| [1] | van Vucht J H N;Kuijpers F A;Bruning H C A M .[J].Philips Research Reports,1970,25:133-140. |
| [2] | Vivet S;Joubert J M;Knosp B et al.[J].Journal of Alloys and Compounds,2003,356-357:779-783. |
| [3] | Feng F;Geng M;Northwood D O .[J].International Journal of Hydrogen Energy,2001,26:725-734. |
| [4] | Ambrosio R C;Ticianelli E A .[J].Journal of Power Sources,2002,110:73-79. |
| [5] | Ayari M.;Paul-Boncour V.;Lamloumi J.;Percheron-Guegan A. .Magnetic properties of LaNi3.55Mn0.4Al0.3Co0.75-xFex (x = 0, 0.35) compounds before and after electrochemical cycles[J].Journal of Magnetism and Magnetic Materials,2002(2):850-853. |
| [6] | Percheron-Guégan A;Lartigue C;Achard J C et al.[J].Journal of the Less-Common Metals,1980,74:1-12. |
| [7] | Lartigue C;Percheron-Guégan A;Achard J C .[J].Journal of THE LESS-COMMON METALS,1980,75:23-29. |
| [8] | 李丽,吴锋,陈实,陈人杰.LaNi5-xCox合金电子结构的第一性原理分析[J].物理化学学报,2006(11):1331-1335. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%