研究了采用丙烯腈-丁二烯-苯乙烯树脂(ABS),高聚合度聚氯乙烯(HPVC)为主体材料,丙烯酸酯类共聚物改性剂(ACR)为增容剂,并配以其它助剂制备ABS/HPVC合金.实验结果表明,选择ABS 75,HPVC 25,ACR 2,重质CaCO3＜10及适量助剂,可以制备性能较好的ABS/HPVC合金.以ACR为增容剂,同时加入NBR,能够大大提高ABS/HPVC合金的冲击强度.ACR对ABS/HPVC合金的增容效果同PVC(S-700)相近,但优于CR.
参考文献
| [1] | Paul D;Newman S.Polymer Blends[M].New York:Academic Press,1978 |
| [2] | Olagoke Olabisi;Lloyd M Robeson;Montgomery T. Shaw.Polymer-Polymer Miscibility[M].New York:Academic Press,1979 |
| [3] | 吴本仁.[J].合成树脂及塑料,1989(ZK):52. |
| [4] | 谢荣化.塑料购销手册[M].北京:中国物资出版社,1994:1220-1223. |
| [5] | Deanin R D;Moshar C .[J].Polymeric Preprints(American Chemical Society Division of Polymer Chemistry),1974,15(01):403. |
| [6] | Pavan A;Ricco T;Rink M .[J].Materials Science and Engineering,1980,45:201. |
| [7] | Pavan A;Ricco T;Rink M .[J].Materials Science and Engineering,1980,48:9. |
| [8] | 蔡碧华,邹承沂,黄鸿智.热稳定剂对ABS改性硬PVC稳定性及流动性的影响[J].塑料科技,1986(02):16-22. |
| [9] | Kulshreshtha A K;Pandey G C;Xavier S F et al.[J].European Polymer Journal,1989,25(09):925-927. |
| [10] | 杨国文;丁小明.[J].高分子材料科学与工程,1994(06):114. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%