利用场发射电镜及能谱仪研究了取向电工钢薄、厚板坯铸锭中不同区域的析出相差异,确定了MnS、AlN及Fe3C的析出顺序和形貌特征。结果表明AlN以先析出的MnS为形核核心,形成粗大微米级的复合析出相。针状Fe3C既可以在复合析出相表面形成也可以在基体中单独出现,主要受冷却速度的影响。在1250℃保温1～2 h,AlN、Fe3C均可完全回溶,但部分MnS仍不回溶。MnS尺寸随着保温时间延长而增大。导致热轧板中沿轧向分布的粗大MnS,减弱了粒子钉扎力。
Precipitates in thin and thick slabs of electrical silicon steel were investigated by means of field emission SEM and EDS analysis.The precipitation sequence and the morphology of MnS,AlN and Fe3C particles were identified.AlN particles are observed to be nucleated on surface of MnS forming micron-meter-sized complex particles.Acicular Fe3C can precipitate on surface of the complex MnS/AlN particles or directly from matrix depending on cooling rate of the slabs.After holding at 1250 ℃ for 1-2 h,AlN and Fe3C particles are dissolved into matrix,whereas some MnS remained un-dissolved and the average size of MnS particles increased with the holding time.The coarse un-dissolved MnS particles evolved into strings of large particles along rolling direction leading to the reduction of pinning force.
参考文献
| [1] | 卢风喜.日本取向硅钢板坯低温加热的研制现状[J].钢铁研究,1996(06):54-59. |
| [2] | 曹树卫,申勇,孙江美.浅析电工钢的生产现状及技术发展[J].轧钢,2008(05):35-38. |
| [3] | 朱业超,毛炯辉,王若平,乔学亮.析出相质点对取向硅钢二次再结晶的影响[J].金属热处理,2009(06):29-32. |
| [4] | 夏兆所;康永林;倪献娟 .等,板坯加热温度对低温技术取向电工钢抑制剂与磁性能的影响[J].北京科技大学学报（自然科学版）,2009,31(04):439-444. |
| [5] | 汪玲玲,杨平,毛卫民.Hi-B钢中抑制剂的析出行为[J].材料科学与工程学报,2010(02):194-198. |
| [6] | Masamitsu WAKOH;Takashi SAWAI;Shozo MIZOGUCHI .Effect of S Content on the MnS Precipitation in Steel with Oxide Nuclei[J].ISIJ International,1996(8):1014-1021. |
| [7] | Kang, YB;Kim, HS;Zhang, J;Lee, HG .Practical application of thermodynamics to inclusions engineering in steel[J].The journal of physics and chemistry of solids,2005(2/4):219-225. |
| [8] | Wriedt H A;Hu H .The solubility product of manganese sulfide in 3Pct silicon-Iron at 1270 to 1670K[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1976,7:711-715. |
| [9] | Cheng L.M.;Hawbolt E.B. .Modeling of Dissolution, Growth, and Coarsening of Aluminum Nitride in Low-Carbon Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(8):1907-1916. |
| [10] | 雍崎龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006:406. |
| [11] | 娄德春;崔昆;吴晓春 等.硫化锰夹杂物的热变形行为[J].钢铁研究学报,1996,6(08):11-14. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%