以硝酸锌(Zn(NO_3)_2·6H_2O)、氢氧化钠(NaOH)为原料,在不同水热温度下(60℃、80℃、100℃、120℃、150℃、200℃)制备了不同形貌的氧化锌粉体(ZnO).运用X射线衍射仪(XRD)、扫描电镜(SEM)、紫外一可见漫反射仪以及光化学反应仪对其进行了表征.结果表明,随着水热温度的升高,氧化锌的结晶越来越完善,形貌也由球状变化到椭球状、片状再到六棱柱.氧化锌粉体在波长为200～400nm的紫外光范围内具有很强的吸收,在可见光区域的吸收很弱.光催化降解模拟实验表明,80℃下所制备的氧化锌的催化效果最好.
ZnO powders are prepared by the hydrothermal method at different temperatures (60℃, 80℃, 100℃ , 120℃, 150℃ and 200℃) using Zn(NO_3)_2·6H_2O, NaOH as reactants. The powders are characterized by X-ray diffraction( XRD), scanning electron microscopy(SEM). UV-vis diffuse reflectance spectrometer and photochemical reaction instrument The results show that the crystallinity of powders increases with the increase of temperature and their morphology also change from spherical to ellipsoidal, sheet and then to hexagonal prism. A strong absorption appears in the ultraviolet region between 200nm and 400nm, but in the visible light region, the absorption is weak. Through the photocatalysis decomposed simulation experiment, it is found that the powders which prepared at 80 C own the best photocatalytic activity.
参考文献
| [1] | 陈崧哲,张彭义,祝万鹏,刘福东.可见光响应光催化剂研究进展[J].化学进展,2004(04):613-619. |
| [2] | 周建伟,黄建新,王金娜,李洁.纳米ZnO/膨润土光催化降解亚甲基蓝研究[J].应用化工,2008(09):1063-1066. |
| [3] | 贺北平;王占生;张锡辉 .半导体光催化有机物的研究现状及发展趋势[J].环境科学,1994,15(03):80. |
| [4] | E.Yassitepe;H.C.Yatmaz;C.Ozturk .Photocatalytic efficiency of ZnO plates in degradation of azo dye solutions[J].Journal of Photochemistry and Photobiology, A. Chemistry,2008(1):1-6. |
| [5] | 吴海宝;莉晓耒 .太阳能-TiO_2:非均相光催化氧化染料污水脱色研究[J].中国环境科学,1997,17(01):93. |
| [6] | Yuxin Wang;Xinyong Li;Ning Wang .Controllable synthesis of ZnO nanoflowers and their morphology-dependent photocatalytic activities[J].Separation and Purification Technology,2008(3):727-732. |
| [7] | Chakrabarti S;Dutta B K .Photocatalytic degradation of model textile dyes in wastewater using ZnO asemiconductor catalyst[J].Journal of Hazardous Materials,2004,112(1-3):269. |
| [8] | C.C. Chen;C.S. Lu;Y.C. Chung;J.L. Jan .UV light induced photodegradation of malachite green on TiO_2 nanoparticles[J].Journal of hazardous materials,2007(3):520-528. |
| [9] | 张艳辉,田彦文,赵迎宪,危凤.半导体氧化锌的制备及其光催化性能研究[J].兵器材料科学与工程,2008(01):60-63. |
| [10] | Chiing-Chang Chen .Degradation pathways of ethyl violet by photocatalytic reaction with ZnO dispersions[J].Journal of Molecular Catalysis A:Chemical,2007,264(1-2):82. |
| [11] | 张光友,彭清涛,苏苏,徐文国.纳米氧化锌光催化降解偏二甲肼污水研究[J].导弹与航天运载技术,2008(03):54-56. |
| [12] | Akyol M Bayramoglu .Photocatalytic degradation of Remazol Red F3B using ZnO catalyst[J].Journal of Hazardous Materials,2005,124(1-3):241. |
| [13] | Hariharan C .Photocatalytic degradation of organic contaminants in water by ZnO nanoparticles: Revisited[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2006(1):55-61. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%