采用三点弯曲法测试了单向和三维四向碳纤维增强的两种沥青基碳/碳(C/C)复合材料(1D-C/C和3D-C/C)在室温及1 800℃高温时的弯曲性能,分析了增强体结构、温度对C/C复合材料弯曲性能的影响,并探讨了其弯曲断裂时的界面机制.结果表明:3D-C/C的弯曲模量高于1D-C/C的,但其抗弯强度却明显低于1D-C/C的;1ID-C/C的弯曲断裂呈脆性断裂,而3D-C/C的弯曲断裂则表现出明显的假塑性特征;对同一种增强体结构的沥青基C/C复合材料,在1 800℃时的弯曲性能高于其在室温时的.
参考文献
| [1] | Schmidt DL;Theibert LS;Davidson KE .Unique applications of carbon-carbon composite materials. II[J].SAMPE Journal,1999(4):51-63. |
| [2] | 李贺军.碳/碳复合材料在航空领域的应用研究现状[J].材料工程,1997(08):8. |
| [3] | C. Blanco;E. Casal;M. Granda .Influence of fibre-matrix interface on the fracture behaviour of carbon-carbon composites[J].Journal of the European Ceramic Society,2003(15):2857-2866. |
| [4] | V.E.Yudin;M.Ya.Goykhman;K.Balik;P.Glogar;P.Polivka;G.N.Gubanova;V.V.Kudryavtsev .Carbon/carbon composites based on a polyimide matrix with coal tar pitch[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(9):1427-1433. |
| [5] | Tzeng SS.;Pan HH. .Densification of two-dimensional carbon/carbon composites by pitch impregnation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):127-134. |
| [6] | 孙乐民,李贺军,张守阳.沥青基炭/炭复合材料的弯曲断裂特征[J].新型炭材料,2001(03):28-31,41. |
| [7] | 熊翔,黄伯云,李江鸿,吴凤秋.准三维C/C复合材料的弯曲性能及其破坏机理[J].航空材料学报,2006(04):88-91. |
| [8] | 刘皓,李克智,李贺军,卢锦花,翟言强.中间相沥青基碳/碳复合材料的组织与性能[J].材料工程,2006(05):21-24. |
| [9] | 袁辉 .碳/碳复合材料刚度与强度预测模型研究[D].南京航空航天大学,2009. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%