通过SF6 + CO2气体保护,在大气环境下制备了Mg-12Gd-2Y-0.5Sm-0.5Sb-0.5Zr镁合金,采用HRTEM方法研究了合金225℃时效过程中析出相的组织转变.结果发现,合金时效析出序列为:S.S.S.S→β"相→β'相→β1相→β相,合金内β’析出相呈三角阵列均匀分布,TEM研究显示β’相具有周期结构.
参考文献
| [1] | Smola B.;Stulikova I.;von Buch F.;Mordike BL. .Structural aspects of high performance Mg alloys design[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1-2 Special Issue SI):113-117. |
| [2] | 李克杰,李全安.Sm对AZ61合金力学性能的影响[J].稀土,2012(01):28-32. |
| [3] | 张清,李全安,井晓天,张兴渊.钇在耐热镁合金中的应用[J].稀土,2011(02):71-75. |
| [4] | K.Y. Zheng;J. Dong;X.Q. Zeng .Effect of precipitation aging on the fracture behavior of Mg-11Gd-2Nd-0.4Zr cast alloy[J].Materials Characterization,2008(7):857-862. |
| [5] | 肖阳,张新明,邓运来.Mg-9Gd-4Y-0.6Zr析出相在高温拉伸中的相变[J].特种铸造及有色合金,2007(11):829-831. |
| [6] | S.M. He;X.Q. Zeng;L.M. Peng .Microstructure and strengthening mechanism of high strength Mg-10Gd-2Y-0.5Zr alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):316-323. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%