用稻壳为硅源和成孔剂,以Nd2O3为添加剂,在1350 ℃烧成了多孔堇青石陶瓷.利用XRD分析了试样在烧结过程中的物相变化,利用SEM观察了烧结试样的显微结构,并测定了烧结试样的抗弯强度、气孔率.结果表明:与未掺Nd2O3的试样相比,掺杂3 wt%Nd2O3后,烧结试样的气孔率无明显变化,但其抗弯强度增加了约4倍,且堇青石的形成温度显著降低.
参考文献
| [1] | Mio Terada;Keizou Kawamura;Isao Kagomiya .Effect of Ni substitution on the microwave dielectric properties of cordierite[J].Journal of the European Ceramic Society,2007(8/9):3045-3048. |
| [2] | Isabel Santacruz;Rodrigo Moreno;Joao B. Rodrigues Neto .Preparation of Cordierite Materials with Tailored Porosity by Gelcasting with Polysaccharides[J].International journal of applied ceramic technology,2008(1):74-83. |
| [3] | Yuichi Kobayashi;Katsuhiro Sumi;Etsuro Kato .Preparation of dense cordierite ceramics from magnesium compounds and kaolinite without additives[J].Ceramics International,2000(7):739-743. |
| [4] | 曾令可,李得家,刘艳春,王慧,程小苏,刘平安,税安泽.片状结构堇青石粉体制备的研究[J].人工晶体学报,2009(01):138-142. |
| [5] | 张华,胡娟,周万城,罗发.堇青石质蜂窝陶瓷的制备[J].硅酸盐学报,2004(01):24-28. |
| [6] | 王耀明,薛友祥,李勇,孟宪谦,李杰,张联盟.高温烟气净化用多孔堇青石陶瓷支撑体材料的研制[J].硅酸盐学报,2005(10):1262-1265. |
| [7] | 谢志勇,梁辉,徐明霞,徐廷献.溶胶-凝胶法制备堇青石粉体的固相反应过程和烧结性的研究[J].无机材料学报,2004(04):779-783. |
| [8] | Sen Mei;Juan Yang;J. M. F. Ferreira .Colloidal processing of cordierite-based glass-ceramics[J].International journal of inorganic materials,2001(8):1249-1252. |
| [9] | 薛向欣,张淑会,段培宁.工业固体废弃物作为合成Si基陶瓷原料的开发与利用[J].硅酸盐通报,2005(02):72-75. |
| [10] | 穆柏春,孙旭东.稀土氧化物对钛酸铝陶瓷显微结构和力学性能的影响[J].耐火材料,2003(05):274-276,281. |
| [11] | 俞泽民,孙永,吴叶伟.复合稀土掺杂对β-Sialon陶瓷组织与力学性能影响[J].哈尔滨理工大学学报,2008(06):108-110. |
| [12] | 杨南如;岳文海.无机非金属材料图谱手册[M].武汉:武汉工业大学出版社,2000:207. |
| [13] | Cristina Ghitulica;Ecaterina Andronescu;Oana Nicola .Preparation and characterization of cordierite powders[J].Journal of the European Ceramic Society,2007(2/3):711-713. |
| [14] | Giovanni Bruno;Sven Vogel .Calculation of the Average Coefficient of Thermal Expansion in Oriented Cordierite Polycrystals[J].Journal of the American Ceramic Society,2008(8):2646-2652. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%