用电化学方法研究聚羧酸系和萘系减水剂对模拟混凝土孔隙液中钢筋和混凝土试样中钢筋腐蚀行为的影响．结果表明，两种减水剂对模拟孔隙液中钢筋的腐蚀基本没有明显的抑制作用，但适量的减水剂可以提高混凝土的致密性，从而抑制钢筋腐蚀．通过对浸泡在2．5mol／LNaCl溶液中的混凝土试样进行比较得知，0．1％-0．3％的聚羧酸系减水剂对混凝土中钢筋腐蚀的抑制作用大于0．2％含量的萘系减水剂，并对其抑制机理进行了初步探讨．
The effect of polycarboxylic and naphthalene superplasticizer on the corrosion behavior of rebar steel in simulated concrete pore solutions and concrete was studied by electrochemical techniques. The results indicated that two kinds of water reducer have little effect on the corrosion inhibition of rebar steel in the simulated concrete pore solutions. However, the decrease of corrosion rate of the rebar within reinforced concrete may be resulted from the decrease of porosity and the increase of density of the concrete due to the addition of proper amount of water reducer. It was found that the addition of polycarboxylic type water-reducer in a range of 0.1% to 0.3% was more effective than that of 0.2% naphthalene water reducer in reducing the corrosion rate of reinforcing steels within reinforced concrete immersed in 2.5 mol/L sodium chloride solution. The mechanism of this phenomenon was preliminarily discussed.
参考文献
| [1] | 苏力军,刘昆鹏,闫国婷等.高效减水剂作用机理及研究进展[J].河北建工,2005,(6):1. |
| [2] | Sakai E, Ishida A, Ohtta A. New trends in the develop- ment of chemical admixtures in Japan [J]. J.Adv. Concr. Technol., 2006, 4(2): 221. |
| [3] | 张洪雁.聚羧酸系高效减水剂对水泥水化性能的影响[J].河南建材,2009,(4):97. |
| [4] | 陈红岩.减水剂对水泥浆体水化性能和孔结构影响的试验研究[J].山东建材,2007,(2):16. |
| [5] | 李平辉,王罗强,刘跃进.萘系高效减水剂的合成与应用研究[J].应用化工,2009,38(5):757. |
| [6] | Li L, Sagues A A. Chloride corrosion threshold of rein- forcing steel in alkaline solutions-cyclic polarization be- havior[J]. Corrosion, 2002, 58(4): 305. |
| [7] | 胡融刚,黄若双.氯离子侵蚀下钢筋在混凝土中腐蚀行为的EIS研究[J].物理化学学报,2003,19(1):46. |
| [8] | 姚志雄,胡红梅,宋明佳等.聚羧酸系减水剂与萘系减水剂的性能比较[J].福建建材,2008,(6):9. |
| [9] | 赵铁军.混凝土渗透性[M].北京:科学出版社,2006:62. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%