将0.5 g初始铸态Al-21%Si合金真空封装于14 mm的石英管中,分别在750、800、850和900℃温度下重熔并保温不同时间后水冷,采用光学显微镜分析Al-21%Si合金凝固组织。结果表明：Al-21%Si合金在750～850℃重熔保温20 min后初晶硅比初始铸态合金中的更大,但随着重熔温度的升高,初晶硅的颗粒尺寸逐渐减小,900℃温度下重熔时效果最好;在750℃重熔后初晶硅反而变粗,保温时间对初晶硅颗粒的尺寸影响不明显;在相对较慢的石英管水冷条件下,Al-21%Si合金中的共晶硅比初始铸态组织中的共晶硅更加细小;在750～900℃温度范围内保温不同的时间后,初晶硅的颗粒尺寸基本在25～43μm范围内波动;在800、850和900℃保温时均出现了不同生长程度的五瓣星形初晶硅组织。
As-cast Al-21% alloy with the weight of 0.5 g was encapsulated into a 14 mm evacuated quartz tube,and then the quartz tubes were heated at 750,800,850 and 900 ℃ for different time.The solidification microstructure of the treated Al-21%Si alloy was analyzed by optical microscopy.The results show that when overheated at 750-850 ℃ for 20 min,the primary Si is larger than that in the as received alloy.But the size of primary Si in the Al-21%Si alloy gradually decreases with the increasing of temperature,and the solidified alloy with finest primary Si is achieved at 900 ℃.While overheated at 750 ℃,the primary Si grows bigger than that in the as received alloy,and the effect of holding time on the size of primary Si is quite little.The eutectic Si in the alloy becomes smaller than that in the as received alloy because of lower cooling velocity.Most of the primary Si is with the size of 25-43 μm after overheating at 750-900 ℃ for different holding time.Five petal star-shaped primary Si with different growth level is observed for the alloy after overheating at 800,850 and 900 ℃,respectively.
参考文献
| [1] | 胥锴,刘徽平,袁帮谊,王甫.过共晶铝硅合金变质处理的研究进展[J].热加工工艺,2009(03):32-35. |
| [2] | 彭涛.内燃机活塞材料的发展与前景[J].山西科技,2007(03):91-92,103. |
| [3] | 潘连明,朱正锋,张国荣,周斌,章正晓.Al-Si系铸造铝合金材料的研究[J].机车车辆工艺,2007(01):5-7. |
| [4] | 邱亚东.铝硅系铸造铝合金的晶粒细化处理[J].金属热处理,2010(11):79-80. |
| [5] | 高波,郝仪,王震,涂赣峰,石为喜,李世伟,郝胜智,董闯.过共晶铝硅合金Al-17.5Si强流脉冲电子束表面改性[J].材料热处理学报,2010(09):115-118. |
| [6] | R. G. Guan;F. R. Cao;L. Q. Chen;J. P. Li;C. Wang .Dynamical solidification behaviors and microstructural evolution during vibrating wavelike sloping plate process[J].Journal of Materials Processing Technology,2009(5):2592-2601. |
| [7] | 潘金生;仝健民;田民波.材料科学基础[M].北京:清华大学出版社,1998 |
| [8] | 刘相法;边秀房;马家骥.铝合金组织遗传现象及其利用的研究[J].铸造,1994(10):18-22. |
| [9] | Mondolfo L F;Barlock J G .Effect of superheating on structure of some aluminum alloys[J].Metal1 Trans B,1975,6(04):565-572. |
| [10] | 陈光,蔡英文,李建国,傅恒志.熔体热处理研究及其应用[J].河北科技大学学报,1998(01):6-12. |
| [11] | 魏朋义;傅恒志 .熔体温度处理对快凝Al-Si过共晶合金条带微观组织及性能的影响[J].金属学报,1996,32(08):817-822. |
| [12] | Gui M C;Jia J;Song G S et al.blicrostructure of A1-Si alloys rapidly solidified from the different temperature melts[J].Journal of Materials Science and Technology,1999,15(03):225-228. |
| [13] | Murray J L;McAlister A J .AI-Si(Aluminum-Silicon)[J].Bulletin of Alloy Phase Diagrams,1984,5(01):36-37. |
| [14] | Touloukian Y S;Powell R W;Ho C Y.Thermophysical Properties of Matter[M].IFI/Plenum,New York-Washington,1970 |
| [15] | D.皮茨;L.西索姆;葛新石.传热学[M].北京:科学出版社,2002 |
| [16] | 桂满昌;贾均;李庆春 .五瓣星状初晶硅形核机制[J].金属学报,1996,32(11):1177-1183. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%