采用图象分析软件分析研究了Fe-24Mn-0.5C TWIP钢在拉伸过程中孪晶数量随真应变的变化规律.结果表明:试验钢在拉伸过程中随着真应变的增加,孪晶数量明显增加,到真应变为3.7×10-1时,几乎整个奥氏体晶粒内都充斥着形变孪晶.另外研究表明,孪晶产生的门槛应变值εc与应变速率ε有关,应变速率越小,孪晶产生门槛值εc越小.

参考文献

[1] 栗原雄毅;近藤博史;小松干也 等.现代汽车板的质量控制与成型性[N].日产技报,1991-5-29(16).
[2] 唐荻,米振莉,陈雨来.国外新型汽车用钢的技术要求及研究开发现状[J].钢铁,2005(06):1-5.
[3] 风佩华 .从福特汽车用钢看汽车板的发展[J].钢铁研究,1998,14(01):59.
[4] Grassel O.;Frommeyer G.;Meyer LW.;Kruger L. .High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development - properties - application[J].International Journal of Plasticity,2000(10/11):1391-1409.
[5] Fmmmeyer G;Brvx U;Neumann P .Supra-ductile and high-strength manganese-TRIP/TWIP steels for high energy absorption purpoees[J].ISU International,2003,43(03):438.
[6] Cotes S;Sale M;Fernandez G A .Fcc/hcp martensItic transformation in the Fe.Mn system:experimental and thermodynamic analysis of phase stability[J].Metal Mat Trans,1995,26(04):1957.
[7] Sleedwyk A W .1/2(111)screw dislosations and nucleation of{112}<111>twins in the bcc lattice[J].Philosophical Magazine,1963,8(03):1467-1486.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%