In Situ observation of deformation and fracture for superalloy GH169 under combined fatigue-creep action is made by using high temperature metalloscope,it is shown that under the test conditions the deformution takes place by merely of slipping,twinning and grain houndary sliding,and the mode of failure depends on the microstructure of specimen. lntergranular cracks arise.from W-type voids produced by the stress concentration at triple point which could not be relaxed by the interior deformation of grains and the local deformathm region along grain bounaries.And the crack propagation mechanism is the nucleation,growth and linkage of carities at the grain boundaries.Transgranular cracks form from deformatiom damages within the grain,and its propagation mechanism is shear rupture along the slip phme.