本文采用室温直流磁控溅射Fe-Si组合靶的方法,并通过后续退火温度的优化得到了单一相高质量的β-FeSi2薄膜.结果表明,在本实验条件下得到的未掺杂的β-FeSi2薄膜在室温下是n型导电的,其电学特性存在一个退火温度的最优点:800 ℃.而且在这个最佳温度点上,在Si(111)衬底上外延得到的薄膜载流子迁移率比在Si(100)上高出了一倍多.在上述研究的基础上,采用p-Si(111)单晶片作为外延生长β-FeSi2薄膜的衬底,并通过退火温度和薄膜厚度的优化制备出了国内第一个n-β-FeSi2/p-Si异质结太阳电池,其Jsc=7.90 mA/cm2 ,Voc=0.21 V,FF=0.23,η=0.38%.
参考文献
| [1] | Darakchieva V.;Surtchev M.;Goranova E.;Baleva M. .Structural and optical analysis of beta-FeSi2 thin layers prepared by ion-beam synthesis and solid-state reaction[J].Physical Review.B.Condensed Matter,2000(19):13057-13063. |
| [2] | McKinty CN.;Kirkby KJ.;Homewood KP.;Edwards SP.;Shao G.;Valizadeh R. Colligon JS. .The properties of beta-FeSi2 fabricated by ion beam assisted deposition as a function of annealing conditions for use in solar cell applications[J].Nuclear Instruments and Methods in Physics Research, Section B. Beam Interactions with Materials and Atoms,2002(0):179-182. |
| [3] | Liu ZX;Osamura M;Ootsuka T;Kuroda R;Fukuzawa Y;Otogawa N;Nakayama Y;Makita Y;Tanoue H .Effect of a Fe3Si buffer layer for the growth of semiconducting beta-FeSi2 thin film on stainless steel substrate[J].Journal of Crystal Growth,2007(1):82-86. |
| [4] | Liu Z X;Wang S N;Naotaka O.A Novel β-FeSi2 Thin Film Solar Cell Fabricated by Sputtering[A].Osakn,Japan,2003 |
| [5] | Mahmoud S;Keita N;Kazuhiro N et al.Low-temperature Annealing of n-type β-FeSi2/p-type Si Hererojunctions[J].Japanese Journal of Applied Physics,2008,47:3444-3446. |
| [6] | 聂冬,李晓娜,董闯.β-FeSi2半导体薄膜与Si基体取向关系的研究[J].材料热处理学报,2002(03):59-64. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%