以河南永城无烟煤为原料、KOH为活化剂制备了高比表面积的煤基活性炭,采用低温N_2吸附法对活性炭的比表面积、孔容及孔径分布进行了表征,并对其用作双电层电容器电极材料的电化学性能进行了系统测试.在KOH与煤的质量比为4:1、活化温度为800℃、活化时间为1h的条件下制备出的活性炭其比表面积高达3224m~2/g,总孔容达1.76cm~3/g,中孔率为57.95%.该活性炭电极在3mol/L KOH电解液中的比电容高达324F/g,且具有良好的循环性能,当电流密度为40mA/g时,经1000次循环后,比电容保持率超过92%,且其漏电流很小.
High specific surface area coal-based activated carbons are prepared from Yongcheng anthracite using KOH as activator. The specific surface area, pore volume and pore size distribution of activated carbons are characterized by low temperature nitrogen adsorption. The electrochemical performance of activated carbons electrode material for electric double layer capacitor is tested by constant current charge-discharge, alternating current impedance and cyclic voltammetry. The result indicates that high specific surface area coal-based activated carbons can be prepared under the condition of the ratio of KOH to anthracite being 4 : 1, activation temperature being 800℃ and activation time being 1h, and the specific surface area is 3224m~2/g, total pore volume is 1.76cm~3/g and mesoporosity is 57.95%. In the 3mol/L KOH electrolyte, the specific capacitance of activated carbons electrode material is 324F/g, and it has excellent cyclic performance and low leakage current. The residual specific capacitance is more than 92% after 1000 cycles under the current density of 40mA/g.
参考文献
| [1] | 袁国辉.电化学电容器[M].北京:化学工业出版社,2006:23. |
| [2] | 张传祥,张睿,成果,谢应波,詹亮,乔文明,凌立成.煤基活性炭电极材料的制备及电化学性能[J].煤炭学报,2009(02):252-256. |
| [3] | Grazyna Gryglewicz;Ewa Lorenc-Grabowska;Grzegorz Lota;Elzbieta Frackowiak .Effect of pore size distribution of coal-based activated carbons on double layer capacitance[J].Electrochimica Acta,2005(5):1197-1206. |
| [4] | 李晶,赖延清,李劼,刘业翔.超级电容器用高比表面活性炭的制备与电化学表征[J].材料与冶金学报,2008(01):33-38. |
| [5] | Conway B E;陈艾;吴孟强;张绪礼.电化学超级电容器科学原理及技术应用[M].北京:化学工业出版社,2005:547. |
| [6] | T. Morishita;Y. Soneda;T. Tsumura .Preparation of porous carbons from thermoplastic precursors and their performance for electric double layer capacitors[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(12):2360-2367. |
| [7] | 沈曾民;张文辉;张学军.活性炭材料的制备与应用[M].北京:化学工业出版社,2006:91. |
| [8] | Zhang CX;Long DH;Xing BL;Qiao WM;Zhang R;Zhan L;Liang XY;Ling LC .The superior electrochemical performance of oxygen-rich activated carbons prepared from bituminous coal[J].Electrochemistry communications,2008(11):1809-1811. |
| [9] | 王晓峰 .电化学超电容器的研究[D].北京科技大学,2001. |
| [10] | 刘希邈,张睿,詹亮,张丽明,凌立成.活性炭前处理对双电层电容器性能的影响[J].电子元件与材料,2007(01):52-55. |
| [11] | A. Laforgue;P. Simon;J.F. Fauvarque .Hybrid Supercapacitors Based on Activated Carbons and Conducting Polymers[J].Journal of the Electrochemical Society,2001(10):A1130-A1134. |
| [12] | 张丽明 .有机系超级电容器的电极材料改性及其组装工艺[D].华东理工大学,2007. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%