以八乙烯基低聚倍半硅氧烷（OVPS）为交联剂,通过溶液共聚制备了聚N-异丙基丙烯酰胺有机/无机杂化水凝胶（P（OVPS-co-NIPAM））,研究了其溶胀、消溶胀和再溶胀及药物缓释行为。结果表明,所有P（OVPS-co-NIPAM）杂化水凝胶的平衡溶胀率SR均随温度升高而降低。20℃,5-P（OVPS-co-NIPAM）杂化水凝胶在去离子水中的SR与常规水凝胶P（MBA-co-NIPAM）相同,但在生理盐水中的SR,前者明显大于后者。随着OVPS含量的增加,杂化水凝胶的SR、再溶胀和消溶胀速率均逐渐下降。5-P（OVPS-co-NIPAM）杂化水凝胶的载药率和累积释药率均高于常规水凝胶P（MBA-co-NIPAM）。此外,P（OVPS-co-NIPAM）杂化水凝胶的药物释放速率均高于常规水凝胶,而且20℃时随OVPS含量增加,释药加快。
A series of organic-inorganic hybrid hydrogels（P（OVPS-co-NIPAM）） based on（N-isopropylacrylamide）（NIPAM） using octavinyl polyhedral oligomeric silsesquioxane（OVPS） as the crosslinker were synthesized by solution free radical copolymerization.The influence of OVPS content on the swelling,deswelling and reswelling behaviors in deionized water and normal saline,as well as the drug release behavior with norfloxacin as the model drug were investigated.The results show that the equilibrium swelling ratio（SR） of all P（OVPOSS-co-NIPAM） hydrogels exhibits temperature dependence.The SR of 5-P（OVPS-co-NIPAM） hybrid hydrogel in water at 20 ℃ is basically same with that of the traditional hydrogel using N,N′-methylenebisacrylamide（MBA） as the crosslinker（P（MBA-co-NIPAM））,while the SR of the former in normal saline is larger than that of the latter.The SR and the rates of deswelling and reswelling of P（OVPS-co-NIPAM） hydrogels decrease when the OVPS content increasing.The drug release on norfloxacin reveals that 5-P（OVPS-co-NIPAM） hydrogel possesses higher drug loading ratio and cumulative drug release ratio than P（MBA-co-NIPAM）.Furthermore,the drug release rates of all the P（OVPS-co-NIPAM） hydrogels are also higher than that of P（MBA-co-NIPAM） and increase with the OVPS contents increasing at 20 ℃.
参考文献
| [1] | Todd R. Hoare;Daniel S. Kohane .Hydrogels in drug delivery: Progress and challenges[J].Polymer,2008(8):1993-2007. |
| [2] | Ozturk N;Girotti A;Kose GT .Dynamic cell culturing and its application to micropatterned, elastin-like protein-modified poly(N-isopropylacrylamide) scaffolds.[J].Biomaterials,2009(29):5417-5426. |
| [3] | 刘红宇,杨建国,吴承佩.N-异丙基丙烯酰胺共聚物/粘土纳米复合水凝胶的合成及性能[J].高分子材料科学与工程,2005(02):114-117. |
| [4] | Ronald H. Baney;Maki Itoh;Akihito Sakakibara;Toshio Suzuki .Silsesquioxanes[J].Chemical Reviews,1995(5):1409-1430. |
| [5] | 张晓静,韩喜妞,方少明,李亚东,张忠厚,闫春绵.八乙烯基多面体低聚倍半硅氧烷-N-异丙基丙烯酰胺共聚物有机-无机杂化水凝胶的合成与表征[J].高分子学报,2010(08):1023-1029. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%