以天然鳞片石墨、CrO3、HClO4为原料,采用化学氧化法制备石墨层间化合物(GIC);研究了反应物用量、反应时间、反应温度对石墨层间化合物膨胀容积的影响.结果表明:按石墨∶三氧化铬∶高氯酸(质量比)=1∶0.3∶5,反应温度30℃,反应时间60min的条件,可制得膨胀容积为555mL·g-1的石墨层间化合物.采用FTIR、XRD、TG等技术对石墨层间化合物的组成、结构进行表征和分析得知:石墨层间的插入物为ClO4-、Cr2O72-.GIC性能特点测试结果说明:所制GIC具有低能耗性能、良好的真空安定性、较好的8毫米波动态衰减效果.
参考文献
| [1] | 康飞宇.石墨层间化合物的研究与应用前景[J].新型碳材料,1991(03):89-97. |
| [2] | Tzeng SS.;Ko TH.;Wang PL. .Effects of processing parameters on the structure and amount of intercalation of copper chloride-graphite intercalation compounds[J].Journal of Materials Science,2001(2):497-501. |
| [3] | Savos' Kin M V;Yaroshenko A P .Stabilities of graphite nitrate by intercalation of organic compounds[J].Theoretical and Experimental Chemistry,2004,40(02):92-97. |
| [4] | V.V. Avdeev;N.E. Sorkina;N.V. Maksimova .Synthesis of Ternary Intercalation Compounds in the Graphite-HNO_3-R(R=H_2SO_4,H_3PO_4,CH_3COOH) Systems[J].Inorganic materials,2001(4):366-371. |
| [5] | 高林,龚银香,马玲.膨胀次数对天然鳞片膨胀石墨微结构的影响[J].新型炭材料,2006(02):139-143. |
| [6] | Michio INAGAKI,Tomoya NAGATA,Taisuke SUWA,Masahiro TOYODA.膨胀石墨对各种油类的吸附动力学[J].新型炭材料,2006(02):97-102. |
| [7] | Uwe Kron;Klaus Moller;Ernest Shulz .Pyrotechnic smoke generator for camouflage purposes[P].US,5656794,1997. |
| [8] | 乔小晶,张同来,任慧,张建国.爆炸法制备膨胀石墨及其干扰性能[J].火炸药学报,2003(01):70-73. |
| [9] | 吴昱,尹喜凤,崔建林,武湃.可膨胀石墨在爆炸分散型发烟剂中的应用[J].火工品,2004(02):27-29,35. |
| [10] | 伍士国,徐铭,李澄俊,陈作如.膨胀石墨对8mm波动态衰减性能的影响因素研究[J].火工品,2005(02):1-5. |
| [11] | 伍士国 .可膨胀石墨瞬时膨化与衰减8毫米波动态特性研究(WU Shi-guo.Instantaneous expansion of expansible and the 8mm wave dynamic attenuation characteristic[D].Nanjing:Nanjing University of Science and Technology,2004.)[D].南京:南京理工大学,2004. |
| [12] | Skowronski JM. .ELECTROCHEMICAL FORMATION AND STABILITY OF CRO3-HCLO4-GRAPHITE BI-INTERCALATION COMPOUNDS[J].The journal of physics and chemistry of solids,1996(6/8):695-701. |
| [13] | 魏兴海,张金喜,史景利,郭全贵,要立中.无硫高倍膨胀石墨的制备及影响因素探讨[J].新型炭材料,2004(01):45-48. |
| [14] | Richrad A N;Rondld O K.Infrared Spectra of Inorganic Compounds[M].New York:Wiey,1983 |
| [15] | 吴瑾光.近代傅立叶红外光谱技术及应用(WU Jing-guang.Technology and Application of Modern FTIR Spectroscopy[M].Beijing:Science and Technology Literature Press,1994.)[M].北京:科学技术文献出版社,1994 |
| [16] | 马礼敦.高等结构分析[M].上海:复旦大学出版社,2003:382-384. |
| [17] | 张瑞军,刘建华,沈万慈.石墨层间化合物阶结构的标定方法[J].炭素,1998(02):5-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%