本文以SiO2作为增强材料,制备了SiO2/环氧树脂灌封材料,研究了不同的SiO2含量和热处理工艺条件对灌封材料性能的影响.实验发现,SiO2的加入对环氧树脂灌封材料的拉伸强度和体积电阻率有显著影响,SiO2含量为3%时环氧树脂灌封材料的拉伸强度达到最大值,并且其体积电阻率亦达到最大值;随着固化温度的提高,SiO2/环氧树脂灌封材料的体积电阻率不断减小,力学性能则先升后降,在固化温度为150℃时其力学性能最好.实验结果表明:SiO2含量为3%,固化温度为150℃时,SiO2/环氧树脂灌封材料的综合性能最好,其拉伸强度为1.6MPa,弹性模量为0.44GPa,体积电阻率为3.26×1013(Ω·cm).
参考文献
| [1] | Luis Casta#er;Vicente Jiménez;Manuel Domínguez .A conduction-convection design for liquid flow sensing[J].Sensors and Actuators, A. Physical,1998(1/3):131-137. |
| [2] | Raman VI;Palmese GR .Design and characterization of nanoporous polymeric materials via reactive encapsulation of a chemically inert solvent[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2004(1/3):119-125. |
| [3] | 赵善雷,霍登伟,叶红齐,崔志明.氢氧化铝对环氧灌封料黏度的影响[J].热固性树脂,2005(06):18-20. |
| [4] | Lin YS;Ting JM;Chou TC;Li CC;Huang JL .Determining adhesion and hermeticity of the interface between encapsulation polymer and insulating layer of micro-sensing chips via a capacitance-voltage technique[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2007(17):6827-6832. |
| [5] | 郭艳宏."绿色"电器灌封材料的研制[J].化学工程师,2005(12):14-15. |
| [6] | 付东升,张康助,孙福林.E-39D环氧树脂灌封材料性能研究[J].中国胶粘剂,2005(01):25-27. |
| [7] | 哈恩华,寇开昌,陈立新.环氧灌封材料的研究进展[J].化工进展,2003(10):1057-1060. |
| [8] | 哈恩华,寇开昌,朱修波,颜录科.纳米SiO2/环氧树脂灌封材料的研究[J].材料导报,2004(02):95-97. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%