以Li2CO3为锂源,葡萄糖为C源,与高密度前驱体FePO4混合,采用高温固相反应法合成高密度的锂离子电池正极材料LiFePO4/C复合材料.采用X射线衍射、电子扫描显微镜和恒电流充放电对制得的LiFPO4进行了研究.结果表明,合成材料结晶完整,为均一的橄榄石型结构.C的含量在很大程度上影响LiFePO4的密度,当C的含量为3.0%(质量分数)时,所制正极材料LiFePO4/C的振实密度可达到2.14g/cm3,0.1C放电容量为121.5mAh/g,体积比容量达到260.OmAh/V.
参考文献
| [1] | Padhi AK.;Goodenough JB.;Nanjundaswamy KS. .PHOSPHO-OLIVINES AS POSITIVE-ELECTRODE MATERIALS FOR RECHARGEABLE LITHIUM BATTERIES[J].Journal of the Electrochemical Society,1997(4):1188-1194. |
| [2] | Takahashi M.;Tobishima S.;Takei K.;Sakurai Y. .Reaction behavior of LiFePO4 as a cathode material for rechargeable lithium batteries[J].Solid state ionics,2002(3/4):283-289. |
| [3] | Macneil D D;Zhonghu L;Zhaohui C et al.[J].Power Sources,2002,108(1-2):A8-A14. |
| [4] | Shoufeng Y;Peter Y Z;Whittinggham M S et al.[J].Electrochem Commut,2001,3(09):A505-A508. |
| [5] | Takahashi M;Ohtsuka H;Akuto K et al.[J].Electro-chem Soc,2005,152:A899-A904. |
| [6] | 肖政伟,胡国荣,杜柯,彭忠东,邓新荣.高密度锂离子电池正极复合材料LiFePO4/C[J].中国有色金属学报,2007(12):2040-2045. |
| [7] | 李军,赖桂棠,黄慧民,李大光,夏信德.高比能LiFePO4的制备及性能研究[J].电化学,2007(04):403-406. |
| [8] | 于春洋,潘志红.以球形Li3PO4制备球形LiFePO4[J].北京联合大学学报（自然科学版）,2007(03):75-78. |
| [9] | Ying Jierong;Lei Min;Jiang Changyin et al.[J].Journal of Power Sources,2006,158:543-549. |
| [10] | Gao Xuguang;Hu Guorong;Peng Zhongdong et al.[J].Chinese Chemical Letters,2007,18:1256-1260. |
| [11] | 汤宏伟,朱志红,常照荣,陈中军.高密度锂离子正极材料前驱体Ni0.8Co0.2（OH）2的制备[J].功能材料,2007(10):1717-1719. |
| [12] | 汤宏伟,朱志红,常照荣,陈中军.高密度锂离子电池正极材料LiNi0.8Co0.2O2合成的研究[J].功能材料,2007(06):945-946,951. |
| [13] | Chang Zhaorong;Chen Zhongjun;Wu Feng et al.[J].Electrochimica Acta,2008,53:5927-5933. |
| [14] | 周宗子,朱刚.磷酸铁锂材料及其动力电池产业化现状及前景[J].船电技术,2007(04):257-260. |
| [15] | 肖政伟,胡国荣,杜柯,彭忠东,邓新荣.高密度锂离子电池正极复合材料LiFePO4/C[J].中国有色金属学报,2007(12):2040-2045. |
| [16] | 张宾,林成涛,陈全世.电动汽车用LiFePO4/C锂离子蓄电池性能[J].电源技术,2008(02):95-98. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%