为了改善钢管内衬陶瓷层的韧性,在铝热剂中分别添加ZrO2,Al2O3,SiO2进行改性,采用离心自蔓延高温合成工艺制备了钢管内衬陶瓷层,研究了添加剂对陶瓷层形貌、结构和性能的影响.结果表明:加入ZrO2或Al2O3可以改变陶瓷层的组织结构,使Al2O3由树枝状晶变为等轴晶;加入SiO2可在Al2O3枝晶间隙形成网状Ca2 Si化合物,提高陶瓷层的硬度;加入ZrO2可以显著改善陶瓷层的断裂韧性,加入SiO2次之,而加入Al2O3则降低了陶瓷层的断裂韧性.
参考文献
| [1] | Wenjun Xi;Sheng Yin;Hoyi Lai .Microstructure and mechanical properties of stainless steel produced by centrifugal-SHS process[J].Journal of Materials Processing Technology,2003(1/3):1-4. |
| [2] | Z. Du;H. Fu;H. Fu .A study of ceramic-lined compound copper pipe produced by SHS-centrifugal casting[J].Materials Letters,2005(14/15):1853-1858. |
| [3] | Q.S. Meng;S.P. Chen;J.F. Zhao .Microstructure and mechanical properties of multilayer-lined composite pipes prepared by SHS centrifugal-thermite process[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):332-336. |
| [4] | 杨永利 .10米长陶瓷内衬复合管的制造方法及专用离心机[P].中国,0071005568.1,2007-11-07. |
| [5] | 吕珺,金志浩,郑治祥,丁厚福.氧化铝基陶瓷复合材料表面裂纹的自愈合[J].无机材料学报,2001(03):535-540. |
| [6] | 李大梅,尤显卿,许育东,刘宁,石敏.氧化铝基陶瓷材料断裂韧性的测量与评价[J].硬质合金,2004(04):231-236. |
| [7] | 赵忠民,叶明惠,杜心康,王建江,张龙.SHS陶瓷内衬复合管合成及陶瓷致密化技术[J].材料科学与工程,2002(01):120-124,74. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%