DIMENSIONAL INSTABILITY OF LD31 Al ALLOY WELDMENTS AT ROOM TEMPERATURE AND AFTER THERMAL CYCLES

金属学报(英文版), 2004, 17(1): 64-70.

^1, , ^2, , ^3, , ^4, , ^5,

1.National key Laboratory of Advanced Welding Production and Technology, Harbin Institute of Technology,Harbin 150001, China

2.National key Laboratory of Advanced Welding Production and Technology, Harbin Institute of Technology,Harbin 150001, China

3.National key Laboratory of Advanced Welding Production and Technology, Harbin Institute of Technology,Harbin 150001, China

4.National key Laboratory of Advanced Welding Production and Technology, Harbin Institute of Technology,Harbin 150001, China

5.Harbin First Mechanical Production Factory, Harbin 150080, China

DIMENSIONAL INSTABILITY OF LD31 Al ALLOY WELDMENTS AT ROOM TEMPERATURE AND AFTER THERMAL CYCLES

Keywords： LD31 aluminum alloy

The unstable dimensional distortion of LD31 aluminum alloy weldments at room temperature and after thermal cycles was studied by use of light interference and CMM(three-coordinate measuring machines). At the same time, distortion mechanism was analyzed from the viewpoint of mechanics and microstructure. Experimental results show that there exists obvious difference of unstable dimensional distortion between LD31 welded specimens under two conditions mentioned above. Under room temperature, dimensional variation of welded specimens will decrease gradually and finally tends to be stable during 200h after welding. The relative elongation of welded specimen is 3.0×10-5; After thermal cycles, distortion of welded specimen is much larger than that at room temperature. After 11 thermal cycles, the dimension will tend to be stable. Dimensional unstable distortion of weldments mainly results from temperature condition, microstructure variation and relaxation of welding residual stress.

参考文献

[1]	N N Prokhorov.Physical Process in Metal Welding[M].T.2.M.:Metallurgy,1976:599.
[2]	X H Ke .[J].Aerospace Technology(in Chinese),1996,12(05):10 .
[3]	C Wu;Y X Peng.[J].Space Navigation Journal(in Chinese),1993(01):14.
[4]	Y H Teng .[J].Space Navigation Journal(in Chinese),1994,5(05):13.
[5]	V I Sagalevich.Dimensional Stability of Welded Joint and Its Structure[M].Mockov,1986:10.
[6]	T E Malinkina;H A Markaqev;B A Kovton .[J].Welding Production,1998,8(08):17.
[7]	J Li.Master Thesis[M].哈尔滨:哈尔滨工业大学,1988:24.
[8]	D L Su.Mechanical Properties of Metals[M].北京:机械工业出版社,1987:224.
[9]	B B Qirnihe;E A Shmelewa.[J].Weld Production(in Russian),1999(05):47.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

DIMENSIONAL INSTABILITY OF LD31 Al ALLOY WELDMENTS AT ROOM TEMPERATURE AND AFTER THERMAL CYCLES

参考文献