采用固相二步合成法,通过在预烧粉料中添加LiBiO2,制备出一种低温烧结的Pb0.95Sr0.05(Zr0.54Ti0.46)O3压电陶瓷材料.LiBiO2的添加具有降低烧结温度同时提高陶瓷性能的优点.实验结果表明:适量的LiBiO2掺杂,可形成过渡液相烧结,使烧结温度降低到950～1050℃,比未添加时的烧结温度低240～340℃.当w(LiBiO2) =1.0％,陶瓷达到最佳压电性能:压电应变常数d33=425 pC/N,平面机电耦合系数kp=57.62％,退极化温度Td=350℃,相对介电常数ε33T/ε0=1543,介电损耗tanδ=0.0216,剩余极化强度Pr=35.51 μC/cm2,体积密度p =7.45g/cm3.该材料可应用于低温共烧的叠层压电器件中.
参考文献
| [1] | 朱宏亮,孙清池,刘海燕,李建华.低温烧结PZT-O.5%PbO·WO3压电陶瓷[J].硅酸盐学报,2006(04):476-478. |
| [2] | Zhang W;Eitel R E .Low-Temperature Sintering and Properties of 0.98PZT-0.02SKN Ceramics with LiBiO2 and GuO[J].Journal of American Geramic Scoiety,2011,94(10):3386-3390. |
| [3] | 周桃生,彭炜,尚勋忠,郑克玉,邝安祥.低温烧结改性PbTiO3压电陶瓷材料的研究[J].压电与声光,2001(02):106-109. |
| [4] | R. Mazumder;A. Sen .'Ultra'-low-temperature sintering of PZT: A synergy of nano-powder synthesis and addition of a sintering aid[J].Journal of the European Ceramic Society,2008(14):2731-2737. |
| [5] | 成钧,江民红,刘心宇.K0.5Na0.5NbO3-LiSbO3-BiMnO3无铅压电陶瓷的常压烧结与压电性能[J].中南大学学报（自然科学版）,2010(05):1791-1795. |
| [6] | 杨桂华,周昌荣.BNT-BKT-BiFeO3无铅压电陶瓷的压电性能和退极化温度[J].人工晶体学报,2009(02):335-339. |
| [7] | 江向平,廖军,魏晓勇,张望重,李国荣,陈大任,殷庆瑞.中温烧结 PZN-PZT系陶瓷的压电性能研究[J].无机材料学报,2000(02):281-286. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%