Effect of MgO on Sintering Process and Metallurgical Properties of Sinter

研究了MgO对烧结工艺及烧结矿冶金性能的影响.研究结果表明,在烧结过程中不加或少加MgO,可提高烧结生产效率,获得冷态强度高、软熔带温度区间窄的烧结矿,从而提高高炉软熔带的透气性、降低料柱全压差.为保证高炉渣对MgO含量的要求,以及确保烧结矿低的低温还原粉化率,提出了合理添加MgO的新工艺.

[1]	Matsumura M;Sunahara K;Hoshi M .Effect of Dolomite Sinter Under High Temperature Sinter Condition on Soften Properties[J].CAMP-ISIJ,2004,17:812-816.
[2]	Kenichi HIGUCHI;Masaaki NAITO;Masanori NAKANO .Optimization of Chemical Composition and Microstructure of Iron Ore Sinter for Low-temperature Drip of Molten Iron with High Permeability[J].ISIJ International,2004(12):2057-2066.
[3]	Masanori NAKANO;Masaaki NAITO;Kenichi HIGUCHI .Non-spherical Carbon Composite Agglomerates: Lab-scale Manufacture and Quality Assessment[J].ISIJ International,2004(12):2079-2085.
[4]	Kimura H;Tsukihashi F.Phase Diagram for the Cao-SiO2-Feox System and Melting Behavior[A].Tokyo:MEXT,2003:83-86.
[5]	郎建峰,李振国,张玉柱.MgO对烧结矿质量的影响及MgO与B2O3的交互作用[J].矿产综合利用,2000(01):22-25.
[6]	张玉柱,冯向鹏,李振国,尹海生,田建军,李贵阳,龚树山,张聪山,乔启平,李豪杰.改善低硅烧结矿冶金性能的研究及实践[J].烧结球团,2004(01):4-7.
[7]	Kimura K;Tsukihashi F .Effect of Al2O3 and MgO Addition on Melting Behavior of Sinter[J].CAMP-ISIJ,2004,17:574-577.
[8]	吴贤甫 .降低梅山烧结矿低温还原粉化的研究[D].东北大学,2003.
[9]	沈峰满;杜鹤桂;刘新等.助燃剂对煤粉燃烧等性能的影响[J].东北大学学报(自然科学版),1996,17:167-170.

上一张下一张

计量

作者相关

文章评分