By rheological experimental measurements of SnO2 sol systems derived by the precursor
Tetrabutylorthostannate Sn(OBun)4, it was reported that tear viscosity η, intrinsic viscosity [η] and pH values of the sol solution systems varied dynamically with time. Based on the rheologically dynamic observations, the growth character of SnO2 sol
grains and its structural evolution rule were discussed, and proton H+ production phenomena associated with sol grain growth process were also explained. From
experimental investigations and theoretical discussion, the growth process of SnO_2 sol grains is controlled by a three-stage growth model,
and grain structure keeps invariant during the growth period before sol→gel transformation and sol solution acidity (pH)
influences profoundly the sol grain growth rates.
参考文献
| [1] | Zarzebski Z M, Marton J P. J. Electrochem. Soc., 1976, 123 (7): 199--205c. [2] Zarzebski Z M, Marton J P. J. Electrochem. Soc., 1976, 123 (9): 299--310c. [3] Zarzebski Z M, Marton J P. J. Electrochem. Soc., 1976, 123 (10): 333--346c. [4] Frank G, Kauer E, Kostlin H. Thin Solid Films, 1981, 77: 107--117. [5] Orel B, Lavrencic-stangar U, Crnjak-Orel Z, et al, J. Non-Cryst. Solids, 1994, 167: 272--288. [6] 郭玉忠, 王剑华, 刘荣佩. 稀有金属, 1998, 22: 37--39. [7] 郭玉忠, 王剑华, 刘荣佩. 稀有金属, 1998, 22: 40--44. [8] 王剑华，郭玉忠，刘荣佩. 稀有金属, 1998, 22: 136--138. [9] 刘荣佩, 陈庆华，郭玉忠. 稀有金属, 1998, 22: 132--135. [10] 王剑华，郭玉忠. 材料科学与工艺, 1999, 7 (3): 1--4. [11] 黄瑞安. 溶胶-凝胶法SnO_2 材料制备中溶胶结构表征、演化动力学研究?昆明理大学硕士论文，1999. [12] 郭玉忠, 黄瑞安，王剑华(FUO Yu-Zhong, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 待发表. [13] Pope E T A, Mackenzie J D. J. Non-Cryst. Solids, 1986, 87: 185--197. [14] Flory P J, et al. J. Am. Chem. Soc., 1951, 73: 1904--1908. |