为了研究NaCl溶液浓度对304不锈钢腐蚀过程的声发射特征影响,采用声发射检测技术(AE)及光学显微镜(OM)监测并分析了试样在不同浓度NaCl溶液中腐蚀过程的声发射信号及表面形貌.结果表明,随NaCl溶液浓度增加,试样受腐蚀产生的声发射信号幅度降低,达到最终稳定值的时间先增加后减小,声发射信号幅度范围缩小.在0.1、0.3和0.5 mol·L-1的NaCl溶液浓度下,声发射撞击数累积以线性递增,试样受腐蚀产生的声发射信号振铃计数集聚区较多,0.1和0.5 mol·L-1浓度下的声发射振铃计数集聚区比0.3 mol·L-1多,且持续于整个腐蚀过程.随浓度增加,试样点蚀明显.
参考文献
| [1] | 骆鸿,李晓刚,肖葵,董超芳.304不锈钢在西沙海洋大气环境中的腐蚀行为[J].北京科技大学学报,2013(03):332-338. |
| [2] | K.H. Lo;C.H. Shek;J.K.L. Lai .Recent developments in stainless steels[J].Materials Science & Engineering. R, Reports,2009(4/6):39-104. |
| [3] | 秦丽雁,宋诗哲,张寿禄.光亮退火处理304不锈钢在NaCl溶液中的耐蚀性[J].材料热处理学报,2006(02):98-102. |
| [4] | Jenn-Terng Gau;Po-Han Chen;Hao Gu;Rong-Shean Lee .The coupling influence of size effects and strain rates on the formability of austenitic stainless steel 304 foil[J].Journal of Materials Processing Technology,2013(3):376-382. |
| [5] | G. J. Deng;S. T. Tu;Q. Q. Wang;X. C. Zhang;F. Z. Xuan.Small fatigue crack growth mechanisms of 304 stainless steel under different stress levels[J].International Journal of Fatigue,2014:14-21. |
| [6] | Murr L E;Staudhammer K P;Hecker S S .Effect of strain atate and strain rate on deformation induced transformation in 304 stainless steel,part Ⅱ m icrostructural study[J].Metallurgical Transactions A,1982,13(02):627-635. |
| [7] | 杨瑞成,毕海娟,牛绍蕊,靳塞特,申鹏.温度和Cl-质量分数对304不锈钢耐点蚀性能的影响[J].兰州理工大学学报,2010(05):5-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%