用MBS和SBS协同增韧具有耐高温但又具脆性的无规SMA.研究表明,SMA与MBS和SBS共混时,SMA和MBS的PMMA壳有很好的相容性,与SBS的PS链段部分相容,虽然MBS增韧SMA的效果比SBS好,但却有限.MBS和SBS以合适的比例共同增韧SMA时,合金的缺口冲击强度大于各自单独增韧SMA的相应值,并且当两者比为某一值时出现极大值,该极大值随两者总量提高而增大.电镜观测表明,在合金中MBS以约0.2 μm直径的球状颗粒存在,而SBS以约10 μm的不规则团状物出现.协同增韧效应的产生与MBS和SBS尺寸密切相关.
参考文献
| [1] | 石正金;王荣伟;陈智强 等.[J].上海化工,2001,26(15):18-22. |
| [2] | 王浩,王荣伟.橡胶增韧苯乙烯与马来酸酐共聚物的方法[J].合成树脂及塑料,2001(05):49-51,60. |
| [3] | Tolinski M .[J].Modern Systems,1998,56(06):36-41. |
| [4] | Dharmarajan N;Datta S .[J].POLYMER,1992,33(18):3848-3857. |
| [5] | Hobbs S Y .[J].Polymer Engineering and Science,1986,26:74-81. |
| [6] | Paul D R;Buckhall C B .Polymer Blends Vol. Ⅱ: Performance[M].John Wiley and Sons:New York,2000,2 |
| [7] | Fowler M E;Keskkula H;Paul D R .[J].Polymer,1987,28:1703-1711. |
| [8] | Kishida K;Kitai K;Mohri M .[P].EP:346853,1989. |
| [9] | Moore E R;Lehrer R G;Lyons C E et al.[P].US 3919354,1975. |
| [10] | STRETZ H.A.;CASSIDY P.E.;PAUL D.R. .Blends of Bisphenol A Polycarbonate and Rubber-Toughened Styrene-Maleic Anhydride Copolymers[J].Journal of Applied Polymer Science,1999(6):1508-1515. |
| [11] | Kim J H;Keskkula H;Paul D R .[J].Journal of Applied Polymer Science,1990(40):183-201. |
| [12] | Dekkers M E J;Heikens D .[J].Journal of Applied Polymer Science,1983,28:3809-3815. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%