通过元素分析、性能测试、XRD、SEM和TEM等手段分析了稀土Ce和Y对AZ80镁合金熔炼、组织和力学性能的影响规律。结果表明：在AZ80合金熔炼过程中，添加稀土Y元素能够起到有效除Fe的作用；AZ80合金中分别添加1%(质量分数)的Ce和Y，可以显著细化合金的晶界第二相，并在晶界上分别生成针状的Al11Ce3相和块状的Al2Y相；挤压变形后，Al-RE相在晶界上能够通过阻止位错运动而有效抑制再结晶晶粒长大；挤压+T5处理后，含1%Y的合金具有最好的力学性能，抗拉强度和屈服强度分别达到390和250 MPa，而含1%Ce的合金无论是在挤压态还是T5处理后，其力学性能最低。
The effects of rare-earth Ce and Y on the melting, microstructure and mechanical properties of AZ80 Mg alloys were investigated by elementary analysis, mechanical properties examination, XRD, SEM and TEM. The experimental results show that the content of Fe decreases obviously during alloy melting, and the melting time is shortened when Y is added into AZ80. The as-cast microstructure of AZ80 alloys is refined, and needle-like Al11Ce3 and block-like Al2(Y, Mn) phases generate at grain boundary when 1%Ce and 1%Y (mass fraction) are added into AZ80 alloys. After extrusion, the coarsening of recrystallized grain is depressed by Al-RE phases impeding motion of dislocation at grain boundary. And after extrusion+T5(177℃, 0-30 h) heat-treatment, the maximum tensile strength of AZ80 alloy containing 1%Y is obtained with ultimate tensile stress of 390 MPa and yield stress of 250 MPa.
参考文献
| [1] | MORDIKE BL;EBERT T .Magnesium properties- applications-potential[J].Materials Science and Engineering A,2001,302:37-45. |
| [2] | 师昌绪,李恒德,王淀佐,李依依,左铁镛.加速我国金属镁工业发展的建议[J].材料导报,2001(04):5-6. |
| [3] | 王渠东,丁文江.镁合金研究开发现状与展望[J].世界有色金属,2004(07):8-11. |
| [4] | Tadataka Kaneko;Masami Suzuki .Automotive Applications of Magnesium Alloys[J].Materials Science Forum,2003(Pt.1):67-72. |
| [5] | 陈振华.变形镁合金[M].北京:化学工业出版社,2005:1. |
| [6] | B. Smola;I. Stulfkova;J. Pelcova .Significance of stable and metastable phases in high temperature creep resistant magnesium-rare earth base alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2004(1/2):196-201. |
| [7] | 吴安如,夏长清,董丽君.稀土Ce和Y在ZK60合金中的分布、演变及其对性能的影响[J].稀有金属材料与工程,2007(11):1955-1959. |
| [8] | ROKHLIN L L.Magnesium alloys containing rare earth metals[M].New York:Taylor and Francis,2003:12-13. |
| [9] | F. KHOMAMIZADEH;B. NAML;S. KHOSHKHOOEI .Effect of Rare-Earth Element Additions on High-Temperature Mechanical Properties of AZ91 Magnesium Alloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2005(12):3489-3494. |
| [10] | WANG Jie,ZHOU Ji-xue,TONG Wen-hui,YANG Yuan-sheng.Effect of purification treatment on properties of Mg-Gd-Y-Zr alloy[J].中国有色金属学报（英文版）,2010(07):1235-1239. |
| [11] | 王少武,夏长清,吴安如.稀土铈对AZ31镁合金显微组织和力学性能的影响[J].矿冶工程,2006(04):76-78,82. |
| [12] | 周海涛,曾小勤,刘文法,丁文江,朱燕萍.稀土铈对AZ61变形镁合金组织和力学性能的影响[J].中国有色金属学报,2004(01):99-104. |
| [13] | 吴伟,盛晓方,邹智厚,王珏,陈立佳,刘正.稀土元素Nd在热挤压AZ61镁合金中的作用[J].沈阳工业大学学报,2007(01):24-27. |
| [14] | 张洪杰,孟健,唐定骧.高性能镁-稀土结构材料的研制、开发与应用[J].中国稀土学报,2004(01):40-47. |
| [15] | 吴国华,樊昱,翟春泉,丁文江.稀土La对AZ91D镁合金在NaCl溶液中耐蚀性的影响[J].金属学报,2008(10):1247-1252. |
| [16] | 宋雨来 .稀土改性 AZ91 镁合金组织和腐蚀性能[D].长春:吉林大学,2006. |
| [17] | WANG Y X;FU J W;YANG Y S .Effect of Nd addition on microstructures and mechanical properties of AZ80 magnesium alloy[J].Transactions of Nonferrous Metals Society of China,2012,22(16):1322-1328. |
| [18] | 潘复生;韩恩厚.高性能变形镁合金及加工技术[M].北京:科学出版社,2007:85. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%