将环氧树脂E-44与三乙烯四胺(TETA)形成的加成物接枝到聚天冬酰胺(PAM)大分子链上,形成聚酰胺-胺-环氧梳形接枝聚合物,以丁基缩水甘油醚部分封端,制备了非离子型水性环氧固化剂.研究了PAM接枝该加成物的比率、接枝加成物在加成物中的含量、伯胺封端量对固化剂性能的影响,并与市售水性环氧涂膜性能进行了比较.试验结果表明,多胺加成物接枝率20％、接枝含量25％、伯胺封端量25％的固化剂体系稳定性良好,与现有的市售水性固化剂性能相比,其固化的环氧体系的柔韧性和耐冲击性能有大幅的提高.
参考文献
| [1] | Glass J E.Technology for Waterborne Coatings,Chapter 1[M].Washington D C:American Society,1997 |
| [2] | Shuji Kojima;Yoshiki Watanabe .Development of high performance waterborne coatings Part Ⅰ:Emulsification of epoxy resin[J].Polymer Engineering & Science,2004,5(33):253-259. |
| [3] | 刘志远,朱亚君,王留方,赵宝华,移易.非离子型水性环氧树脂固化剂的合成与性能研究[J].涂料工业,2010(10):47-51. |
| [4] | 赵立英,金平平,刘平安.非离子型水性环氧固化剂的制备与性能[J].高分子材料科学与工程,2014(09):20-23. |
| [5] | Xiaoqing Liu;Yi Wang;Yang Cao .Study of dextrin-derived curing agent for waterborne epoxy adhesive[J].Carbohydrate Polymers: Scientific and Technological Aspects of Industrially Important Polysaccharides,2011(3):1180-1184. |
| [6] | Xiao, XY;Hao, CC .Preparation of waterborne epoxy acrylate/silica sol hybrid materials and study of their UV curing behavior[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2010(1/3):82-87. |
| [7] | Gerlitz;Martin;Ficher et al.Water dilutable amine curing agents for aqueous two component epoxy resin systems[P].US:6653369,2003-11-25. |
| [8] | 邹海良,张亚峰,邝健政,徐宇亮,刘军.水性环氧固化剂及其改性技术[J].热固性树脂,2010(04):53-57. |
| [9] | 陈奕汐,饶秋华.新型水性环氧树脂固化剂合成及性能的研究[J].材料开发与应用,2014(01):58-65. |
| [10] | 柳鑫华,王文静,丁云飞,佟欣佳,赵新强.缓蚀阻垢剂聚天冬氨酸衍生物合成条件的探究[J].工业水处理,2014(01):61-64. |
| [11] | 刘海 .水性环氧涂料制备及防腐性能研究[D].沈阳理工大学,2012. |
| [12] | 石亚军,陈中华,余飞.水性环氧防腐涂料的制备与性能研究[J].电镀与涂饰,2009(04):45-49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%