为提高镍基高温合金抗高温氧化性能,采用两步法制备了内扩散型铬铝涂层与单一渗铝涂层.当保温时间9h、渗铬温度为1080℃、渗铬剂配比为:Cr粉含量为30％、NH4Cl含量为1％、Al2O3含量为69％;渗铝保温时间15 h、温度为750℃、渗铝剂配比为:Al粉含量为10％、NH4Cl含量为1.5％、Al2O3含量为88.5％;热处理保温时间为15 h、温度为800℃时可以得到期望的内扩散型β-NiAl和γ’-NiAl相,涂层组织均匀致密,可显著提高镍基高温合金基体在1100℃的抗高温氧化性能.
参考文献
| [1] | Goward G W.Protective coatings propose,role and design[J].Materials Science and Technology,1986(02):194-200. |
| [2] | 陈为为,何业东.TiAl合金表面机械研磨渗铝涂层的制备及高温性能[J].材料热处理学报,2011(06):138-142. |
| [3] | 田晓东,郭喜平.铌基超高温合金包埋渗铝改性硅化物涂层结构[J].材料热处理学报,2008(05):114-118. |
| [4] | Wang B.;Gong J.;Wang AY.;Sun C.;Huang RF.;Wen LS. .Oxidation behaviour of NiCrAlY coatings on Ni-based superalloy[J].Surface & Coatings Technology,2002(1):70-75. |
| [5] | G. W. Goward .Progress in coatings for gas turbine airfoils[J].Surface & Coatings Technology,1998(1/3):73-79. |
| [6] | Stott F H;Wood G C;Stringer J .The influence of alloying elements on the development and maintenance of protective scales[J].Oxidation of Metals,1995,44:113-145. |
| [7] | Zhang Z G;Gesmundo F;Hou P Y et al.Criteria for the formation of protective Al2O3 scales on Fe-Al and Fe-Cr-A1 alloys[J].Corrosion Science,2006,48:741-765. |
| [8] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001 |