目的：研究高速电弧喷涂 FeCrNi/ Ni 包覆金刚石复合涂层的组织结构和摩擦学特性。方法采用高速电弧喷涂技术在45#钢基体上制备 FeCrNi/ Ni 包覆金刚石复合涂层,并对其进行滑动摩擦磨损研究,利用 SEM,EDS 对涂层的形貌、组织成分进行分析,测定涂层的显微硬度、孔隙率等。结果 FeCrNi/Ni 包覆金刚石复合涂层组织致密,孔隙率较低,呈现典型的层状结构。涂层的摩擦系数随着磨损时间的增加而先增大,再趋于平稳。结论由于涂层中加入了金刚石硬质相,涂层具有较高的显微硬度和优异的耐摩擦磨损性能。
Objective To study the structure and tribological properties of the FeCrNi/ Ni coated diamond composite coating by high-velocity arc sprayed. Methods FeCrNi/ Ni coated diamond composite coating was prepared on 45# steel substrates by high-ve-locity arc sprayed. MMW-1A wear-test machine was used to analyze the tribological properties of the composite coating. Morpholo-gy, composition and cross-section microstructure of the coatings were analyzed by the means of scanning electron microscopy (SEM), and energy dispersive spectrometry (EDS). The microhardness and porosity of coatings were also tested. Results This re-search indicated that the FeCrNi/ Ni coated diamond composite coatings had typical layer structure characteristics and lower porosi-ty. With the increase of sliding time, the friction coefficient of the coatings first increased and then tended to be stable. Conclu-sion The coating had high microhardness and excellent wear resistance because of the addition of ultrohard diamond.
参考文献
| [1] | 董晓焕,张振云,李琼伟,等 . 工艺参数对高速电弧喷涂Al/1Cr13 复合涂层组织结构的影响[J].中国表面工程,2012,25(1):65-70. DONG Xiao-huan,ZHANG Zhen-yun,LI Qiong-wei,et al. Effects of Spray Parameters on Microstructure of High Ve-locity Arc Sprayed Al/1Cr13 Composite Coatings[J]. China Surface Engineering,2012,25(1):65-70.,2012. |
| [2] | 王刚,焦孟旺,李贺,贡泽飞,魏元生,杨红新.热喷涂新技术在发动机减摩性能方面的应用和研究[J].表面技术,2014(01):103-108,130. |
| [3] | LIU Gui-min,ROZNIATOWSKI K J . Quantitative Charac-teristics of FeCrAl Films Deposited by Arc and High-veloci-ty Arc Spraying[J].Materials Characterization,2001,46:99-104.,2001. |
| [4] | KAVIAN C,GOSSETT O,VERNON B,et al . Optimization of the Electric Wire Arc-spraying Process for Improved Wear Resistance of Sugar Mill Roller Shells[J].Surface and Coatings Technology,2007,201(1):185-188.,2007. |
| [5] | 黄林兵,余圣甫,邓宇,戴明辉,徐慧子.电弧喷涂4Cr13涂层预处理工艺及组织与性能研究[J].表面技术,2010(06):26-28,70. |
| [6] | 彭怡刚,吴玉锋 . AZ31 表面电弧喷涂 Al-FeAl 复合涂层的研究[J].热加工工艺,2010,39(18):112-115. PENG Yi-gang,WU Yu-feng. Research on Al-FeAl Compos-ite Coating on AZ31 Surface Prepared by Arc Spray[J]. Hot Working Technology,2010,39(6):26-28.,2010. |
| [7] | 欧献,邓畅光,王日初,毛杰.超音速等离子喷涂工艺参数对Cr2O3涂层硬度的影响[J].表面技术,2014(01):81-85,102. |
| [8] | 徐润生,徐滨士,徐维普.增强相对高速电弧喷涂铁铝复合涂层摩擦学特性的影响[J].机械工程材料,2006(01):16-19. |
| [9] | 齐凤莲,赵民,孙志礼.等离子热喷涂金刚石涂层的摩擦磨损性能研究[J].润滑与密封,2008(02):40-42,59. |
| [10] | 田浩亮,魏世丞,陈永雄, 等 . 高速电弧喷涂 FeCrAl/Ni95Al 复合涂层的性能[J].金属热处理,2013,38(4):92-96. TIAN Hao-liang,WEI Shi-cheng,CHEN Yong-xiong,et al. Properties of FeCrAl/Ni95Al Coating by High Velocity Arc Spraying[J]. Heat Treatment of Metals,2013,38(4):92-96.,2013. |
| [11] | 刘荣祥,周立文,杨玉杰,曹先启.电弧喷涂Ti6Al4V涂层的组织与耐蚀性能研究[J].表面技术,2011(01):14-16,67. |
| [12] | 徐维普,徐滨士,张伟,等 . 高速电弧喷涂 FeAlCr/Ni 包Cr3 C2 复合涂层摩擦学特性[J].中国有色金属学报,2004,14(10):1671-1675. XU Wei-pu, XU Bin-shi, ZHANG Wei, et al. Tribological Properties of High Velocity Arc Sprayed FeAlCr/Ni Wraped Cr3 C2 Coatings[J]. The Chinese Journal of Nonferrous Me-tals,2004,14(10):1671-1675.,2004. |
| [13] | 关长斌,孙丽君 . 化学镀铜对金刚石性能的影响[J].表面技术,1995,24(5):12-14. GUAN Chang-bin, SUN Li-jun. The Effect of Electroless Plated Cu on Properties of Diamond[J]. Surface Technolo-gy,1995,24(5):12-14.,1995. |
| [14] | 高叔轩,刘贵昌,张茹芝,陈野.超声波化学镀的研究进展[J].表面技术,2004(02):1-3. |
| [15] | 王照锋,卢红梅 . 高速电弧喷涂 FeCrNi/CBN 复合涂层的组织与性能[J].材料保护,2007,40(5):37-39. WANG Zhao-feng, LU Hong-mei. Microstructure and Pro-perties of High Velocity arc Spraying FeCrNi/CBN Coatings [J]. Materials Protection,2007,40(5):37-39.,2007. |
| [16] | 王照锋,彭伟 . 高速电弧喷涂 FeCrNi/WC 粉芯丝材的研制与性能研究[J].表面技术,2006,35(5):16-17. WANG Zhao-feng,PENG Wei. Development and Properties Research of High Speed Arc Spraying FeCrNi/WC Cored Wire[J]. Surface Technology,2006,35(5):16-17.,2006. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%