本文研究了石膏掺量对阿利特-硫铝酸钡钙水泥抗硫酸盐侵蚀性能的影响,并与硅酸盐水泥进行了比较;利用XRD,SEM-EDS等测试方法对侵蚀后水泥水化产物的物相组成和形貌进行了分析.研究结果表明:阿利特-硫铝酸钡钙水泥具有良好的抗硫酸盐侵蚀性能.当石膏掺量为5%时,阿利特-硫铝酸钡钙水泥的抗蚀系数达1.31,而硅酸盐水泥的抗蚀系数仅为0.94.石膏对阿利特-硫铝酸钡钙水泥硬化浆体的致密性有较大影响,进而影响水泥的抗硫酸盐侵蚀性能.同时,对阿利特-硫铝酸钡钙水泥的抗侵蚀机理进行了初步分析.
Effect of gypsum content on the sulfate resistance of alite-barium calcium sulphoaluminate cement was investigated. Portland cement was taken for comparison. The composition and microstructure of hardened cement pastes were analyzed by X-ray diffraction and scanning electron microscope. The results show that alite-barium calcium sulphoaluminate cement has better ability of sulfate resistance. The coefficient of resistance to sulfate attack with 5% gypsum addition in alite-barium calcium sulphoaluminate is 1.31, while that in Portland cement is only 0.94. Gypsum can affect the tightness of alite-barium calcium sulphoaluminate cement hardened pastes and further influence the ability of resistance to sulfate attack. At the same time, the mechanism of sulfate resistance of alite-barium calcium sulphoaluminate cement was discussed in this paper.
参考文献
| [1] | 王伟,衣朝华,李仕群,赵发伟,刘飚,胡佳山.新型磷铝酸盐水泥抗硫酸盐侵蚀性能[J].硅酸盐学报,2008(01):82-87. |
| [2] | 程新,芦令超,王来国,常钧,刘福田,陈亚明,叶正茂.高胶凝性阿利特-硫铝酸钙钡矿相体系的研究[J].硅酸盐学报,2004(03):321-326. |
| [3] | 芦令超,常钧,沈叶青,于丽波,程新,刘韩星,袁润章.阿利特-硫铝酸钡钙水泥材料制备技术的研究[J].硅酸盐通报,2004(05):16-19,23. |
| [4] | 芦令超,常钧,沈业青,程新,刘韩星,袁润章.阿利特-硫铝酸钡钙水泥的合成与力学性能[J].硅酸盐学报,2005(07):902-906. |
| [5] | 王来国,芦令超,程新.硅酸盐与硫铝酸盐矿物复合水泥材料的研究进展[J].济南大学学报(自然科学版),2004(01):24-27. |
| [6] | Cheng Xin;Chang Jun;Lu Lingchao .Study on the hydration of Ba-bearing calcium sulphoaluminate in the presence of gypsum[J].Cement and Concrete Research,2004(11):2009-2013. |
| [7] | 张风臣,马保国,谭洪波,蹇守卫.不同环境下水泥基材料硫酸盐侵蚀类型和机理[J].济南大学学报（自然科学版）,2008(01):33-37. |
| [8] | 石明霞,谢友均,刘宝举.水泥-粉煤灰复合胶凝材料抗硫酸盐结晶侵蚀性[J].建筑材料学报,2003(04):350-355. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%