利用高频感应加热膏剂法在Ti6A14V合金表面制备了渗铬层，对渗铬层的厚度、显微组织、化学成分、硬度、结合强度以及摩擦学性婵进行了研究。结果表明：渗铬层厚度可达25μm以上；渗铬后在合金表面形成了由α＋β、CrVO3、（Ti0．88Cr0．12）2O3和TiN相组成的渗铬层；渗铬层的化学成分呈梯度分布，距渗铬层表面25μm处的硬度可达850HV，渗铬层与基体实现了7台金结合，明显提高了基体的摩擦学性能。
A chromized layer was prepared on Ti6A14V alloy surface by high frequency induction heating and paste method, and the thickness, microstructure, chemical composition, hardness, bond strength and tribological property of the chromized layer were studied. The results show that the thickness of the chromized layer was more than 25 μm and the layer composed of α＋β, CrVO3, （Ti0. 88 Cr0.12 ）2 O3 and TiN phases. The chemical composition of chromized layer exhibited gradient distribution. The hardness at a distance of 25μm away from the chromized layer surface reached 850 HV. The chromized layer and the substrate had metallurgical bonding and thus increased obviously the tribological property of the substrate.
参考文献
| [1] | 梁文萍,徐重,缪强,刘小萍,贺志勇.Ti2AlNb双层辉光等离子渗Cr的摩擦磨损性能研究[J].摩擦学学报,2007(02):121-125. |
| [2] | 王小峰,范莹,王振霞,贺志勇.TiAl合金表面等离子渗铬工艺[J].理化检验-物理分册,2008(02):57-60,70. |
| [3] | 徐晋勇,高原,黄伟,恽志东,徐重.表面高Cr高C合金层摩擦性能的研究[J].金属热处理,2007(z1):390-393. |
| [4] | 张高会,张平则,崔彩娥,郭丽娜,潘俊德,徐重.钛合金及其表面处理的现状与展望[J].世界科技研究与发展,2003(04):62-67. |
| [5] | 张平则,李忠厚,贺志勇,徐重,张高会.Ti- 6Al- 4V表面双层辉光离子渗Cr研究[J].兵器材料科学与工程,2005(01):17-20. |
| [6] | 王艳 .离子溅射渗金属的研究[D].大连海事大学,2006. |
| [7] | 高原,芦金斌,徐重.表面高铬高碳合金层的研究[J].化工机械,2003(03):143-146,151. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%