利用光学显微镜和H-800透射电镜研究了不同加热温度和不同保温时间下高强度船板钢奥氏体品粒长大规律.结果表明,该钢在高温加热时具有较好的抗晶粒粗化能力,奥氏体晶粒粗化温度在1250℃左右;在1100℃和1200℃保温时,奥氏体晶粒等温长大规律较好地服从抛物线型经验表达式;随着温度的升高,钢中的第二相质点逐渐减少,当加热至1250℃时,钢中仅存TiN颗粒.
参考文献
| [1] | 沈俊昶,杨才福,张永权,李丽,侯家平.船体结构用高强韧特厚钢板的研究[J].材料开发与应用,2004(05):1-4. |
| [2] | Garcia C;Bartolome M J;Capdevila C et al.Metallo-Graphic Techniques for the Determination of the Austenite Grain Size in Medium-Carbon Micro Alloyed Steels[J].Materials Characterization,2001,46(10):389. |
| [3] | Moona J;Lee J .Prediction for the Austenite Grain Size in the Presence of Growing Particles in the Weld HAZ of Ti-Microalloyed Steel[J].Materials Science and Engineering,2007,459:40. |
| [4] | 陈永,汪喜和,刘胜新,刘国权.微合金钢中奥氏体晶粒长大规律研究[J].热加工工艺,2007(16):4-6. |
| [5] | Gladman T.Grain Refinement in Multiple Micro-Alloyed Steels[A].Warrendale,PA:TMS,1992 |
| [6] | Krauss G;Thompson S .Ferrite Microstructure in Continuously Cooled Low-and-Ultra Low-Carbon Steels[J].ISIJ International,1995,35(06):934. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%