The melt spun ribbons of Al-La-Y-Ni(Fe)quaternary alloys were prepared by a single- roller melt spinning technique in vacuum.Their amorphous nature,mechanical properties and tensile fracture surface morphology were investigated.The experimental results show that amorphous alloys with high strength and good ductility as well as good thermal stability can be achieved in Al-La-Y-Ni(Fe)system,when the alloy contains 85—90 at.-% Al and less than 10 at.-% La+Y.The maximum tensile fracture strength(σ_f) and microhardness(HV)are as high as 760 MPa and 294 DPN,respectively.The as- quenched ribbons can be bent 180 degree without fracturing.The dominant factors for formation of amorphous Al-La-Y-Ni(Fe)are the strong attractive interaction among Al, La,Y and a decrease of melting temperature.