以AM60镁合金和硅为原材料，在原位反应的基础上，采用高能超声处理来改善原位反应的条件，制备出以Mg2Si为增强相的镁基复合材料；采用XRD对复合材料物相进行分析，用光学显微镜对其显微组织进行观察，同时与未施加超声处理的复合材料进行了对比。结果表明：超声作用下原位生成的Mg2Si增强相更加细小，团聚现象得到改善；熔体在高能超声作用下，声空化产生的瞬态高温、高压及声流效应是增强相细化的主要原因。
With AM60 magnesium alloy and silicon as raw materials, based on in-situ reaction using highenergy ultrasonic treatment method to improve the conditions, magnesium matrix composites with Mg2Si as reinforcing phase were synthesized. By means of X-ray diffraction and optical microscopy, the phase and microstructure of the composites were analyzed and observed. It was compared with the composites obtained without ultrasonic treatment. The results show that the Mg2 Si reinforcing phases generated by the ultrasonic in-situ reaction were smaller and the agglomeration phenomenon was improved. The main reasons of the refinement of reinforcing phase were transient high temperature, high pressure and acoustic streaming effect from acoustic cavitation under the high-energy ultrasonic treatment.
参考文献
| [1] | 臧树俊,周琦,马勤,安亮.金属间化合物Mg2Si研究进展[J].铸造技术,2006(08):866-870. |
| [2] | 王连登,傅高升,陈晓,钱匡武.硅对Mg2Si/ZM5复合材料组织和性能的影响[J].特种铸造及有色合金,2003(02):7-10. |
| [3] | 胡勇,闫洪,陈国香,梅楹煜.Si对原位自生Mg2Si/AM60复合材料组织及性能的影响[J].稀有金属材料与工程,2009(02):343-347. |
| [4] | 何柏林,缪燕平.超声波强化处理对AZ91D镁合金组织及性能的影响[J].热加工工艺,2007(12):4-6. |
| [5] | 胡志,闫洪,聂俏,凌李石保.超声法制备纳米SiC颗粒增强AZ61镁基复合材料的显微组织[J].中国有色金属学报,2009(05):841-846. |
| [6] | 郭峰 .镁合金凝固组织的超声细化机制及工艺研究[D].南昌大学,2008. |
| [7] | 胡勇,闫洪,陈国香.原位生成Mg2Si/AM60复合材料的热力学与动力学分析[J].特种铸造及有色合金,2008(03):239-241. |
| [8] | 王俊,陈锋,孙宝德.高能超声在制备颗粒增强金属基复合材料中的作用[J].上海交通大学学报,1999(07):813-816. |
| [9] | 丁加善,赵玉涛,张松利,陈刚.超声化学原位合成（Al2O3+Al3Zr）p/A356复合材料[J].铸造,2008(04):354-358. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%