研究了再结晶退火温度对一次冷轧阴罩带钢显微组织、力学性能和磁性能的影响.结果表明,当退火温度在750℃到810℃时,试样拉伸时没有屈服点延伸,退火温度升高使晶粒长大,这有利于钢板的成形性和磁性能;当退火温度为840℃时,钢板的组织变得不均匀,同时有0.04%的屈服点延伸,这不利于阴罩服役时的形状稳定性.对本阴罩带钢而言,合理的再结晶退火温度为810℃.
参考文献
| [1] | 关海玲 .彩色显像管用阴罩带钢的组织性能研究[D].上海:上海交通大学,2006. |
| [2] | 李俊 .宝钢股份冷轧厂内部报告[R].,2004. |
| [3] | Sato;Taizo;Ueda et al.Material for Shadow Mask,Method for Production thereof,Shadow Mask and Image[P].US 6803712,2004-10-12. |
| [4] | Kim G S;Hwang H G .Method for manufacturing cold rolled shadow mask steel sheet with stacked Annealing[P].US 6193519,2001-3-13. |
| [5] | 李俊;陈守群;姚林龙 等.阴罩带钢及其生产方法[P].CN 01113107.1,2002-1-9. |
| [6] | IEC Standard 404-7-1982.IEC Standard 404-7-1982.Magnetic Materials[S]. |
| [7] | Kim K S;Hwang H G;Kim E Y .Cold rolled steel sheet for shadow mask made by low temperature annealing and mannfaeturing method therefore[P].US 6117253,2000-9-12. |
| [8] | Jeong W C;Park C H;TPark T Y .Cold rolled sheet steel for shadow mask and manufacturing method therefore[P].WO 96/13618,1996-5-9. |
| [9] | A. J. DeArdo .Niobium in modern steels[J].International Materials Reviews,2003(6):371-402. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%