以线性聚苯乙烯(PS)为膜材料,采用Breath Figures法制备了高度规整的蜂窝状结构多孔膜.研究了溶液浓度、环境湿度、气体吹扫速度及不同溶剂对多孔膜结构的影响.结果表明,相比于苯和二氯甲烷,氯仿作为溶剂因其挥发度适宜,PS浓度在20～80mg/mL的铸膜溶液可形成规整的蜂窝状结构多孔膜,且膜孔分布均匀、大小均一；制膜的湿度需高于环境湿度,但随着湿度的增加孔径增大；气体吹扫速度可在400～1000mL/min范围,但吹扫速度较大时孔径略有降低.该膜可作为固定诸如辣根过氧化酶等活性酶的载体,用于酶催化反应.
参考文献
| [1] | Bunz UHF .Breath figures as a dynamic templating method for polymers and nanomaterials[J].Advanced Materials,2006(8):973-989. |
| [2] | Shimomura M;Sawadaishi T .[J].Curr Opin Collid Interface Sci,2001,6(01):11-16. |
| [3] | Beattie D;Wong K H;Williams C et al.[J].Biomacromolecules,2006,7:1072-1082. |
| [4] | Widawski G;Rawiso B;Francois B .[J].Nature,1994,369(02):387-389. |
| [5] | 陈观文,曾一鸣.膜微孔形成方法的研究进展[J].膜科学与技术,2003(04):116-122. |
| [6] | Stenzel M H .[J].Australian Journal of Chemistry,2002,55(04):239-243. |
| [7] | Stenzel-Rosenbaum M H;Davis T P;Fane A G et al.[J].Angewandte Chemie International Edition,2001,40(18):3428-3432. |
| [8] | Peng J;Han Y C;Fu J;at al .[J].Macromolecular Chemistry and Physics,2003,204:125-130. |
| [9] | Wang C;Liu Q;Shao X et al.[J].Talanta,2007,71:178-185. |
| [10] | 申延明,吴静,卢欣,唐杨军,刘丹,李长龙,李天舒.利用Breath Figure法制备具有Honeycomb结构的有机/无机复合膜[J].高等学校化学学报,2009(07):1464-1468. |
| [11] | Maruyama N;Koito T;Nishida J et al.[J].Thin Solid Films,1998,327-329:854-856. |
| [12] | Pitois O;Francois B .[J].the European Physical Journal B,1999,8(02):225-231. |
| [13] | Deutsh M;Vlasov Y A;Norris D J .[J].Advanced Materials,2000,12(16):1176-1180. |
| [14] | Srinivasarao M;Collings D;Philips A et al.[J].Science,2001,292(5514):79-83. |
| [15] | 万灵书,柯蓓蓓,李晓凯,孟祥麟,章路遥,徐志康.聚苯乙烯/聚乙二醇蜂窝状有序膜的制备与表征[J].中国科学B辑,2008(12):1081-1087. |
| [16] | Yu C;Zhai J;Gao X et al.[J].Journal of Physical Chemistry B,2004,108(15):4586-4589. |
| [17] | 于春玲,翟锦,高雪峰,万梅香,江雷,李泽生,李铁津.掺杂态聚苯胺蜂窝状有序多孔薄膜的制备及形成机制的探讨[J].高等学校化学学报,2004(07):1322-1324. |
| [18] | Tian Y;Jiao QZ;Ding HY;Shi YQ;Liu BQ .The formation of honeycomb structure in polyphenylene oxide films[J].Polymer: The International Journal for the Science and Technology of Polymers,2006(11):3866-3873. |
| [19] | Peng J;Han Y C;Yang Y M et al.[J].Polymer,2004,45(02):447-452. |
| [20] | 施特尔马赫.酶的测定方法[M].北京:中国轻工业出版社,1992:276-278. |
| [21] | 王赪胤,冒银道,王德艳,胡效亚.自组装方法制备有序微孔薄膜[J].化学进展,2008(01):105-116. |
| [22] | 孙巍,唐越超,计剑.以Pluronics（R）为第二组分制备聚乳酸蜂窝状规整多孔薄膜[J].高等学校化学学报,2007(07):1388-1392. |
| [23] | 李磊,钟雅文,陈财康,李剑.基于静态呼吸图技术的图案化方法[J].物理化学学报,2010(04):1135-1142. |
| [24] | Nishikawa T.;Ookura R.;Nishida J.;Arai K.;Hayashi J.;Kurono N. Sawadaishi T.;Hara M.;Shimomura M. .Fabrication of honeycomb film of an amphiphilic copolymer at the air-water interface[J].Langmuir: The ACS Journal of Surfaces and Colloids,2002(15):5734-5740. |
| [25] | Tian Y;Ding HY;Jiao QZ;Shi YQ .Influence of solvents on the formation of honeycomb films by water droplets templating[J].Macromolecular chemistry and physics,2006(5):545-553. |
| [26] | 田野,施艳荞,曾一鸣,矫庆泽,王晓琳.高湿度条件下蜂窝孔结构的形成与控制[J].膜科学与技术,2005(05):78-84,91. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%