以廉价的Ti( SO4)2为钛源,采用低温水-溶剂热法一步制得吸附SO2-4的介孔偏钛酸,焙烧后得到介孔SO2-4/TiO2亚微米粉体,研究了反应物浓度、反应温度、溶剂和表面活性剂对样品催化性能的影响,并采用XRD、SEM、FF-IR、N2吸附-脱附和Hammett指示剂法对催化剂进行表征,考察了其光催化性能.结果表明,最佳制备条件为:Ti( SO4)2浓度0.85 mol/L、十二烷基苯磺酸钠(SDBS)浓度0.004 mol/L、反应温度130℃、反应时间20 h、乙醇水混合液为溶剂；所得样品比表面积(BET)为103.67 m2/g、平均孔径6nm、孔容积为0.204 cm3/g,最高酸强度H0=- 12.14,180 min内对亚甲基蓝(MB)降解率达94％.
参考文献
| [1] | Yoshitake H.;Sugihara T.;Tatsumi T. .Preparation of wormhole-like mesoporous TiO2 with an extremely large surface area and stabilization of its surface by chemical vapor deposition[J].Chemistry of Materials,2002(3):1023-1029. |
| [2] | Mahendra P.Kapoor;Yuichi Ichihashi;Koji Kuraoka;Yasuyuki Matsumura .Catalytic methanol decomposition over palladium deposited on thermally stable mesoporous titanium oxide[J].Journal of molecular catalysis, A. Chemical,2003(1/2):303-308. |
| [3] | 戴遐明 .半导体氧化物超细粉末对Cr(Ⅵ)的光催化还原作用研究[J].环境科学,1996,17(06):34-36. |
| [4] | 习海玲,韩世同,左言军,张建宏,杨雷.TiO2光催化降解乙酰甲胺磷[J].环境化学,2008(05):559-564. |
| [5] | Yu JC.;Zhang LZ.;Zheng Z.;Zhao JC. .Synthesis and characterization of phosphated mesoporous titanium dioxide with high photocatalytic activity[J].Chemistry of Materials,2003(11):2280-2286. |
| [6] | 黄涛,张国亮,张辉,许伟,蒋华兵.高性能纳米二氧化钛制备技术研究进展[J].化工进展,2010(03):498-504. |
| [7] | 石建稳,陈少华,王淑梅.多孔纳米氧化钛的制备及其光催化降解罗丹明B[J].人工晶体学报,2010(01):158-162. |
| [8] | 扈玫珑,白晨光,徐盛明,徐刚,邱贵宝.工业钛液直接水解制备球形二氧化钛[J].重庆大学学报,2009(12):1431-1435. |
| [9] | 李继东,蔡亚岐,史亚利,牟世芬,江桂斌.离子型表面活性剂自组装体系在化学中的应用[J].化学进展,2007(10):1606-1611. |
| [10] | 张明俊,沈俊,田从学,张昭.介孔SO2-4/TiO2固体超强酸的制备与表征[J].功能材料,2006(12):1955-1958. |
| [11] | 沈俊,罗妮,张明俊,田从学,张昭.介孔TiO2-SO2-4的合成及表征[J].催化学报,2007(03):264-268. |
| [12] | 苏文悦,陈亦琳,付贤智,魏可镁.SO2-4/TiO2-SiO2固体超强酸的结构及其光催化性能[J].高等学校化学学报,2002(07):1398-1400. |
| [13] | 苏文悦,付贤智,魏可镁.SO2－4表面修饰对TiO2结构及其光催化性能的影响[J].物理化学学报,2001(01):28-31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%