通过现场暴晒实验,研究T2紫铜和H62黄铜在西沙海洋大气环境下分别暴晒3/4、1、2、和4 a的长周期腐蚀行为.利用SEM观察表面、截面腐蚀产物以及去除腐蚀产物后的腐蚀形貌,并分别用EDS及XRD对腐蚀产物的元素分布及相组成进行分析.结果表明,紫铜和黄铜均发生了严重的腐蚀,4 a 内其平均腐蚀速度分别为5.90和5.88μm/a;紫铜表面发生了均匀腐蚀,腐蚀产物由内层致密的Cu2O及外层的Cu2Cl(OH)3组成;黄铜发生了明显的脱锌腐蚀,腐蚀产物主要为ZnO和Zn5(OH)8Cl2?2H2O,腐蚀产物层下的基体为20~50μm厚度不等的脱锌层.
@@@@Long period corrosion behavior of copper T2 and brass H62 after atmospheric exposure in Xisha islands for 3/4, 1, 2 and 4 a was investigated. The surface and cross-section morphologies, the elements distribution and phase compositions of corrosion products were observed by SEM, EDS and XRD, respectively. The results indicate that copper and brass undergo severe corrosion. The average corrosion rates for copper and brass in 4 a are 5.90 and 5.88 μm/a, respectively. The corrosion type of copper is uniform corrosion, a double layer structure is observed:a compact Cu2O inner layer and a porous Cu2Cl(OH)3 outer layer. Dezincification processes with zinc preferentially dissolution are evident in brass, the zinc-rich corrosion products ZnO and Zn5(OH)8Cl2?2H2O are the predominating patina. Under the corrosion products, there exists a layer of pure copper originated from dezincification with the thickness of 20?50μm.
参考文献
| [1] | 张生龙,尹志民.高强高导铜合金设计思路及其应用[J].材料导报,2003(11):26-29. |
| [2] | RICE D W;PETERSON P;RIGBY E B;PHIPPS P B P CAPPELL R J TREMOUREUX R .Atmospheric corrosion of copper and silver[J].Journal of the Electrochemical Society,1981,128(02):275-284. |
| [3] | Rosa Vera;Diana Delgado;Blanca M. Rosales .Effect of atmospheric pollutants on the corrosion of high power electrical conductors - Part 2. Pure copper[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(5):2329-2350. |
| [4] | MENDOZA A R;CORVO F;GóMEZ A;GóMEZ J .Influence of the corrosion products of copper on its atmospheric corrosion kinetics in tropical climate[J].Corrosion Science,2004,46(05):1189-1120. |
| [5] | I.T.E. Fonseca;R. Picciochi;M.H. Mendonca;A.C. Ramos .The atmospheric corrosion of copper at two sites in Portugal: a comparative study[J].Corrosion Science,2004(3):547-561. |
| [6] | Nú?EZ L;REGUERA E;CORVO F;GONZáLEZ E VAZQUEZ C .Corrosion of copper in seawater and its aerosols in tropical island[J].Corrosion Science,2005,47(02):461-484. |
| [7] | Goidanich, S.;Brunk, J.;Herting, G.;Arenas, M.A.;Odnevall Wallinder, I..Atmospheric corrosion of brass in outdoor applications. Patina evolution, metal release and aesthetic appearance at urban exposure conditions[J].Science of the Total Environment,2012:46-57. |
| [8] | SKENNERTON G;NAIRN J;ATRENS A .Atmospheric corrosion of copper at Heron Island[J].Materials Letters,1997,30(2/3):141-146. |
| [9] | 安百刚,张学元,韩恩厚.沈阳大气环境下纯铜的初期腐蚀行为[J].金属学报,2007(01):77-81. |
| [10] | 杨敏,王振尧.铜的大气腐蚀研究[J].装备环境工程,2006(04):38-44. |
| [11] | 刘琼,王庆娟,杜忠泽.铜在自然环境中的腐蚀研究[J].新技术新工艺,2008(08):80-82. |
| [12] | 陈杰,郑弃非,孙霜青,温军国.海军黄铜HSn62-1的长期大气腐蚀行为[J].中国有色金属学报,2011(03):577-582. |
| [13] | LI T;LI X G;DONG C F;CHENG Y F .Characterization of atmospheric corrosion of 2A12 aluminum alloy in tropical marine environment[J].Journal of Materials Engineering and Performance,2009,19(04):591-598. |
| [14] | 郝献超,李晓刚,肖葵,董超芳.Q235钢在西沙大气环境中的初期腐蚀行为[J].中国腐蚀与防护学报,2009(06):465-470. |
| [15] | 吴军,李晓刚,董超芳,张三平,周建龙.紫铜T2和黄铜H62在热带海洋大气环境中早期腐蚀行为[J].中国腐蚀与防护学报,2012(01):70-74,79. |
| [16] | Corrosion of metals and alloys-Corrosivity of atmospheres-Classification[S].,1992. |
| [17] | 曹楚南.中国材料的自然环境腐蚀[M].北京:化学工业出版社,2005 |
| [18] | H. Strandberg;L. -G. Johansson .Some aspects of the atmospheric corrosion of copper in the presence of sodium chloride[J].Journal of the Electrochemical Society,1998(4):1093-1100. |
| [19] | LIAO X N;CAO F H;ZHENG L Y;LIU W J CHEN A N ZHANG J Q CAO C N .Corrosion behavior of copper under chloride-containing thin electrolyte layer[J].Corrosion Science,2011,53(10):3289-3298. |
| [20] | 李勇,朱应禄.黄铜脱锌腐蚀的研究进展[J].腐蚀与防护,2006(05):222-225,262. |
| [21] | 王晓华,林乐耘,刘安生.HSn62-1铜合金海水腐蚀行为特征的扫描电镜研究[J].稀有金属,1998(06):410-413. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%