海工磷酸镁水泥基材料的制备及性能研究

功能材料, 2012, 43(7): 828-834.

海工磷酸镁水泥基材料的制备及性能研究

蒋江波 ^1, , 薛明 ^2, , 汪宏涛 ^3, , 曹巨辉 ^4,

1.后勤工程学院营房管理与环境工程系,重庆401311／92854部队军港处,广东湛江524000

2.后勤工程学院营房管理与环境工程系,重庆401311

3.后勤工程学院化学与材料系,重庆401311

4.后勤工程学院营房管理与环境工程系,重庆401311

基金项目: 后勤工程学院青年基金资助项目(YQ10-43303) 国家自然科学基金资助项目(50672129,50702076)

关键词：海工 , 磷酸镁水泥 , 制备 , 性能

Research on preparation and properties of marine magnesium phosphate cement based materials

Keywords： marine , magnesium phosphate cement(MPC) , preparation , performance

选用海砂、海水制备了海工磷酸镁水泥基材料,研究了该材料的贮存性能,早期强度特性及抗海水侵蚀性能。结果显示磷酸镁水泥有着良好的贮存性能,原材料按一定方式存放360d后,水泥强度降低不超过5%,原材料存放1000d后,水泥强度降低不超过10%;所制备的海工磷酸镁水泥基材料,2h的抗压强度均达到28MPa以上,1d抗压强度已达52MPa以上,凝结时间在25min以内;所制备的海工磷酸镁水泥胶砂抗海水侵蚀性能良好。

We prepared marine magnesium phosphate cement（MPC） based materials by using sea water and sand,then researched the storage performance,the early strength characteristics and the anti-sea erosion performance of this materials.Results show that the magnesium phosphate cement has good storage performance,after the raw materials was stored with certain storage method for 360d,the strength of MPC was decreased less than 5%,and after the raw materials was stored for 1000d,the strength of MPC was decreased less than 10%.The compressive strength of this marine MPC based materials hydrating for 2h was more than 28MPa,the compressive strength of this marine MPC based materials hydrating for 1d had reached more than 52MPa and the setting time was less than 25min.The marine MPC mortar we prepared has good performance against sea erosion.

参考文献

[1]	Kondratova I L;Montes P;Bremner T W .[J].Cement and Concrete Composites,2003,25:483-490.
[2]	Francois L;Thierry S .[J].Cement and Concrete Research,2002,32:1699-1704.
[3]	王成;汪冬冬.[J].水运工程,2010(01):108-112.
[4]	苏祖平,欧阳华林.C50～C60海工耐久混凝土的试验研究[J].桥梁建设,2006(01):19-21.
[5]	施惠生,王琼.掺复合胶凝材料混凝土的抗氯离子侵蚀性能[J].同济大学学报(自然科学版),2004(04):490-493.
[6]	Wagh A S;Strain R;Jeong S et al.[J].Nuclear Mater,1999,265:295.
[7]	Hall DA.;El Jazairi B.;Stevens R. .Effect of water content on the structure and mechanical properties of magnesia-phosphate cement mortar[J].Journal of the American Ceramic Society,1998(6):1550-1556.
[8]	Jiang H;Liang B;Zhang L M .[J].Journal of Building Materials,2001,4(02):196-198.
[9]	Ding Z;Li Z .[J].Cement and Cement Composites,2005,27(01):11-18.
[10]	汪宏涛,钱觉时,王建国.磷酸镁水泥的研究进展[J].材料导报,2005(12):46-47,51.
[11]	姜洪义,张联盟.磷酸镁水泥的研究[J].武汉理工大学学报,2001(04):32-34.
[12]	程麟,盛广宏,皮艳灵,朱成桂.磷渣对硅酸盐水泥的缓凝机理[J].硅酸盐通报,2005(04):40-44.
[13]	支俊秉,张旭.浅谈试验小磨级配对熟料强度的影响[J].水泥,2006(11):22-24.
[14]	赵东镐,王雪晶.增钙渣和混合材与水泥比表面积的关系[J].水泥技术,2001(05):66-68.
[15]	郭俊萍,梁树娟,张秋英,肖忠明.低碱度硫铝酸盐水泥干缩性能影响因素的研究[J].水泥,2010(01):8-11.
[16]	冉斌.利用煤矸石、工业石膏煅烧阿利特-硫铝酸盐水泥熟料[J].水泥,2006(05):14-15.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网