The microstructures and mechanical properties of deformation induced ferrite(DIF)in the low carbon steel Q235 under different deformation temperatures have been investigated systematically.Through deformation induced ferrite transformation(DIFT),ferrite grain can be refined to 3 μm and accounts for above 85% of the overall fraction.Yield strength of DIF(>500 MPa)is increased by up to 100% compared with the conventional low carbon steel.Comparison of rnicrostructure and mechanical properties in the Q235 steel with DIF and tempered DIF microstructure illustrates that the strengthening mechanism of DIF microstructure is the combination of grain boundary strengthening and carbon supersaturated strengthening.Electron back-scattered diffraction(EBSD)analysis and high magnification scanning electron microscopy(SEM)observation denote that high-angle grain boundary among ultrafine ferrite grain and the transformation product of retain austen-ite membrane along ferrite boundaries are responsible for the stability of ferrite grain size during tempering process.Transmission electron microscopy(TEM)analysis demonstrates that the transformation product of retained austenite membrane between ferrite grain boundaries is cementite.
参考文献
| [1] | B. Q. Han;S. Yue .Processing of ultrafine ferrite steels[J].Journal of Materials Processing Technology,2003(1/3):100-104. |
| [2] | N. Tsuji;Y. Ito;Y. Saito;Y. Minamino .Strength and ductility of ultrafine grained aluminum and iron produced by ARB and anealing[J].Scripta materialia,2002(12):893-899. |
| [3] | P.D.Hodgson;M.R.Hickson;R.K.Gibbs .ULTRAFINE FERRITE IN LOW CARBON STEEL[J].Scripta materialia,1999(10):1179-1184. |
| [4] | R. Priestner;Y. M. Al-Horr;A. K. Ibraheem .Effect of strain on formation of ultrafine ferrite in surface of hot rolled microalloyed steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2002(9):973-980. |
| [5] | S. Torizuka;E. Muramatsu;S.V.S. Narayana Murty .Microstructure evolution and strength-reduction in area balance of ultrafine-grained steels processed by warm caliber rolling[J].Scripta materialia,2006(8):751-754. |
| [6] | M. R. Hickson;P. D. Hodgson .Effect of preroll quenching and post-roll quenching on production and properties of ultrafine ferrite in steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1999(1):85-90. |
| [7] | F. J. Humphreys;P. B. Prangnell;J. R. Bowen;A. Gholinia;C. Harris .Developing stable fine-grain microstructures by large strain deformation[J].Philosophical transactions of the Royal Society. Mathematical, physical, and engineering sciences,1999(1756):1663-1681. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%