总结了国内外在管线钢疲劳特性研究方面的进展情况,介绍了在大气及腐蚀环境中管线钢疲劳行为的原因、影响参数.在这些研究结果的基础上,提出了在我国现有实验条件下,研究X70及以上级别管线钢疲劳行为的具有可行性的方法,包括以较高的加载频率代替管线服役过程中的压力波动频率,以及用小尺寸疲劳试样代替全尺寸实物试验.
参考文献
| [1] | 勃洛达夫金ПП;冯亮.埋设管线[M].北京:石油工业出版社,1980:67. |
| [2] | Charles E A;Parkins R N .[J].Corrosion,1995,51(07):518. |
| [3] | 黄淑菊;邓增杰 .[J].焊管,1991,14(03):13. |
| [4] | Suresh S;王中光.材料的疲劳[M].北京:国防工业出版社,1993 |
| [5] | 潘家华.油气管道断裂力学分析[M].北京:机械工业出版社,1989:89. |
| [6] | Martyr J Wilmott.The Role of Pressure and Pressure Fluctuations in the Growth of Stress Corrosion Cracks in Line Pipe Steels[A].Calgary:ASME Press,1998 |
| [7] | 高惠临.管线钢的组织、性能、行业[M].西安:陕西科学技术出版社,1995 |
| [8] | Wang SH.;Chen WX. .A study on the pre-cyclic-load-induced burst of creep deformation of a pipeline steel under subsequent static load[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):144-151. |
| [9] | Elboujdaini M;Revie R W.Performance of Pipeline Steels in Sour Servuce[A].Calgary (Canada):ASME Press,2000:211. |
| [10] | Parkins R N;Blanchard W K;Delanty B S .[J].Corrosion,1994,50(05):394. |
| [11] | Al Asmi K R;Seibi A C .[J].Engineering Failure Analysis,1998,5(03):195. |
| [12] | Papadopoulos GA.;Vodenicharov SB.;Davidov YA. .Low-cycle fatigue loading of BDS 25G pipeline steel[J].Theoretical and Applied Fracture Mechanics,1998(2):133-137. |
| [13] | Malyukova M G;Timashev S A .[J].ASME Pressure Vessels and Piping PVP,1998,373:99. |
| [14] | Chapetti M D;Otegui J L;Motylicki J .[J].International Journal of Fatigue,2002,24:21. |
| [15] | Mayfeild M E;Maxey W A;Wilkowski G M.Fracture Initiation Tolerrance of Linepipe[A].Houston:American Gas Association,1979:1. |
| [16] | Jones D G .[J].3R International,1982,21(07):347. |
| [17] | Maxey W A.Outside Force Defect Behavior[A].Houston:American Gas Association,1986:1. |
| [18] | Fowler J R;Alexander C R;Kovach P J.[J].Pipeline Eng,1995(69):7. |
| [19] | Kiefner J F;Alexander C R;Fowler J R.Repair of Dents Containing Minor Scratches[A].Houston:American Gas Association,1996:1. |
| [20] | Hagiwara N;Meziere Y;Oguchi N et al.[J].JSME International Journal Series A:Solid Mechanics and Material Engineering,1999,42(04):610. |
| [21] | Baek J H;Kim Y P;KIM W S et al.[J].International Journal of Pressure Vessels and Piping,2001,78(05):351. |
| [22] | Michael J Rosenfeld;Kiefner P E.Investigation of Dent Rerounding Behavior[A].Calgary ( Canada ):ASME Press,1998:299. |
| [23] | 帅健.X52管线钢的低循环频率疲劳裂纹扩展试验[J].焊管,2000(06):20-23. |
| [24] | 韩玉梅;韩恩厚;郑宇礼 .[J].机械强度,1994,16(01):77. |
| [25] | Ahmed T M;Lambert S B;Sutherby R .[J].Corrosion,1997,53(07):581. |
| [26] | 张国军,潘治国,段占军,王荣.X60管线钢腐蚀疲劳裂纹扩展特性[J].石油化工腐蚀与防护,2001(01):53-56. |
| [27] | 顾守仁;姜忠良 .[J].焊管,1988,11(01):29. |
| [28] | Andreikiv O E;Rudavs'kyi D V .[J].Materials Science,1999,35(04):491. |
| [29] | 顾守仁;姜忠良 .[J].焊管,1988,11(03):6. |
| [30] | Newman J C;Raju I S .[J].Engineering Fracture Mechanics,1981,15(1-2):185. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%