研究了U-2.5％Nb合金(质量分数,下同)在相对湿度分别为3.5％、50％、100％、水浸、热水和水蒸气环境,氢气压力分别在0.4,1.0,2.0 MPa条件下的拉伸性能及断口形貌.结果表明:拉伸速率在3×10-5/s时,随环境湿度及氢气压力的增加,U-2.5％Nb合金的抗拉强度降低,规定非比例延伸强度增加,塑性急剧下降.同样在水浸环境,3×10-5/s与1×10-4/s的拉伸速率相比,U-2.5％Nb合金断后伸长率下降约84％,断面收缩率下降约79％.拉伸速率在3×10-5/s时,合金在2.0与0.4 MPa的氢气压力相比,断后伸长率下降约20％,断面收缩率下降约13％.在相对湿度3.5％的环境下,U-2.5％Nb合金试样断口边缘呈韧窝状,有一定的韧性特征.在水浸环境下,试样断口边缘韧窝明显减少,有一定的脆断特征.在水蒸气环境中,试样断口边缘有明显的解理脆断特征.在氢气环境中,试样断口的脆断特征随氢气压力的增加而增强.
参考文献
| [1] | Amato C D;Saraceno F S;Wilson T B .[J].Journal of Nuclear Materials,1964,12(03):291. |
| [2] | Jackson R J .Mechanical Properties of Continuously Cooled Uranium-2.4weight Percent Niobium Alloy:RFP-3040[R].Colorado:Rocky Flats Plant,1981. |
| [3] | Hemperly V C .Effect of the Relative Humidity in Test Atmospheres on U-0.15Ti and U-2.25Nb Alloys:Y-2043[R].Term:Dak Ridge Y-12 Plant,1976. |
| [4] | Hughes A N;Orman S .[J].Journal of Nuclear Materials,1969,33:165. |
| [5] | Beevers C J .[J].Journal of Nuclear Materials,1976,23:10. |
| [6] | Hughes A N;Orman S .[J].Journal of Nuclear Materials,1969,33:159. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%