利用高速电弧喷涂技术在20钢表面分别制备了含稀土和不含稀土的FeMnCrNiAl/Cr3C2涂层。结合光学显微镜、显微硬度、场发射扫描电子显微镜、能谱分析等分析方法对喷涂层的微观组织、显微硬度、结合强度、常温滑动摩擦磨损、高温冲蚀磨损等性能进行研究。结果表明：FeMnCrNiAl/Cr3C2涂层具有较高的结合强度、显微硬度和耐磨性能,加入稀土能降低涂层摩擦系数、提高涂层常温滑动磨损和高温冲蚀磨损性能。
Both RE-containing and RE-free FeMnCrNi/Cr3C2 composite coatings were prepared on 20G steel substrate surface by high velocity arc spraying（HVAS） technology,respectively.Microstructure,micro-hardness,binding strength,sliding friction and wear resistance at ambient temperature,and erosion behaviour at high temperature of the coatings were studied by means of optical microscopy,micro-hardness test,field emission scanning electron microscopy（FESEM） and energy spectrum analysis.The result shows that the binding strength,micro-hardness and wear resistance of the FeMnCrNiAl/Cr3C2 coating are fairly good.The addition of RE-earth element decreases the coatings friction coefficient and improves both the ambient sliding wear resistance and high temperature erosion performance.
参考文献
| [1] | 刘少光,吴进明,张升才,胡小海,荣淑杰,李志章.氮气保护对纳米复合涂层组织与性能的影响[J].浙江大学学报（工学版）,2008(03):493-497. |
| [2] | 罗来马,俞佳,刘少光,孙乃荣,赵琪,郦剑.高速电弧喷涂FeMnCr/Cr3C2涂层的组织与性能[J].材料热处理学报,2009(03):174-177. |
| [3] | 刘少光;温黎;张升才 等.含纳米材料药芯的电弧喷涂丝材的制备方法[P].中国,ZL200410017882.9,2006. |
| [4] | 刘少光;姚继蓬;刘永莉 等.增压式分段加热高温冲蚀磨损试验机[P].中国,ZL200820171371,2009-9-23. |
| [5] | 黄拿灿;胡杜军.稀土表面改性及其应用[M].北京:国防工业出版社,2007:208-211. |
| [6] | 宫文彪,陈光,刘威,孙大千.电弧喷涂Cr3C2增强Fe-Al涂层的组织与性能[J].材料热处理学报,2007(06):139-142. |
| [7] | 张永振.材料的干摩擦学[M].北京:科学出版社,2007:252. |
| [8] | 徐维普,徐滨士,张伟,吴毅雄,孟凡军.高速电弧喷涂Fe-Al/Cr3C2复合涂层的冲蚀特性[J].金属热处理,2005(02):1-4. |
| [9] | 徐维普,徐滨士,张伟,孟凡军,朱子新.高速电弧喷涂FeAlCr/Ni包Cr3C2涂层高温性能[J].金属热处理,2004(07):46-49. |
| [10] | 纪岗昌,李长久,王豫跃,圆田启嗣.喷涂工艺条件对超音速火焰喷涂Cr3C2-NiCr涂层冲蚀磨损性能的影响[J].摩擦学学报,2002(06):424-429. |
| [11] | 王海军,蔡江,韩志海.超音速等离子与HVOF喷涂WC-Co涂层的冲蚀磨损性能研究[J].材料工程,2005(04):50-54. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%