The influence of double aging on the microstructure and mechanical properties of ultrahigh strength steel Aermet 100 was analyzed. Under the double aging, there is no apparent decrease in the strength of steel. However, the impact fatigue life can be prolonged by 35.5% and dynamic fracture toughness be raised by 22.6% respectively, as compared with the normal aging. Based on the observation of microscopic structure, the physical mechanism of the prolongation of impact fatigue life and the enhancement of stability of the reverted austenite, AR, is analyzed further. The results show that this new technique is a breakthrough of combination optimization between strength and toughness for Aermet 100 steel. In the light of the current understanding on this subject, the volume fracture of soften and tough AR formed in process of heat preservation at higher temperature of double aging increases drastically. Moreover, during the treatment of lower temperature of double aging, the carbon separating from the martensitic ferrite will diffuse into AR, resulting that the martensitic brittleness decreases and the stability of AR increases.
参考文献
| [1] | R Ayer;P M Machmeier .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:1943. |
| [2] | E.U. LEE .SCC Path in Forged AerMet 100 Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1995(5):1313-1316. |
| [3] | Bin LING;Ping ZHONG;Bingwen ZHONG;Baozhu GU .[J].Acta Metall.Sin(in Chinese),1995,31A:209. |
| [4] | R hamano .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:127. |
| [5] | M Schmidt;R Hemphill .[J].Scripta Metallurgica et Materialia,1991,25:239. |
| [6] | P M Novotny.Gilbert Speich Symp[A].Warrendale,PA,1992:215. |
| [7] | 凌斌,钟平,钟炳文.新型二次硬化高Co-Ni超高强度钢强韧化机制的研究[J].航空学报,1997(01):44. |
| [8] | G N Haidemenpolous .[D].Ph.D.Thesis,MIT,1988. |
| [9] | L D Wang;C L Chen;M K Kang .[J].Journal of Materials Science and Technology,1999,15(06):583. |
| [10] | Jie SU;Rong LI;Baorong WU .[J].Journal of Iron Steel Res(in Chinese),1995,7(04):67. |
| [11] | Liuding WANG .[D].西北工业大学,2000. |
| [12] | M M Woolfson.An Introduction to X-ray Crystallography[M].Cambridge University Press,Cambridge,1997 |
| [13] | Liuding WANG;Zhenqi GUO;Mokuang KANG;Yicheng HE,Yanqing YANG .[J].材料热处理学报,1998,19(04):49. |
| [14] | C N Sastry;K H Khan;W E Wood .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:676. |
| [15] | E. V. Pereloma;I. B. Timokhina;P. D. Hodgson .Transformation behaviour in thermomechanically processed C-Mn-Si TRIP steels with and without Nb[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(0):448-452. |
| [16] | Weijuan LI;Linxiu DU;Hongmei ZHANG;Xianghua LIU,Guodong WANG .[J].Journal of Iron Steel Res A(in Chinese),2000,12(05):36. |
| [17] | R Hamano .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:127. |
| [18] | S Kocanda;M G Yan;C M Liu.Fatigue and Fracture of Metals[M].上海:上海科学技术出版社,1983:250. |
| [19] | T Y Hsu.Martensitic Transformation and Martensite[M].北京:科学出版社,1980:66. |
| [20] | Mokuang KANG;Ming ZHU.The 6th National Workshop on Solid Transformation[C].Solidification and Their Application,Xi'an,2004 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%