将煤矸石粉经活性改性处理后用作天然橡胶补强填充剂.采用XRD、FT-IR和SEM等手段研究了热处理和偶联剂改性对煤矸石补强天然橡胶性能的影响.煤矸石粉热处理在800℃以内时,天然橡胶硫化胶的拉伸强度随温度升高而增大,当热温度达到900℃时,硫化胶的拉伸强度略有下降.偶联剂改性能显著提高煤矸石的补强性能,当硅烷偶联剂KH-570质量分数≤2％时,天然橡胶的拉伸强度随偶联剂用量增加显著增大;当偶联剂质量分数＞2％时,拉伸强度的增加幅度不明显;而偶联剂质量分数为2％时,硫化橡胶的300％定伸应力达到最大,之后定伸应力随偶联剂质量分数增大而减小.
参考文献
| [1] | 孙刚,刘焕胜.煤矸石资源化利用现状及其进展[J].煤炭加工与综合利用,2012(03):53-56. |
| [2] | Li B;Gong G;Xie BH;Yang W;Yang MB;Lai SM .Fracture behaviour of polypropylene sheets filled with epoxidized natural rubber (ENR)-treated coal gangue powder[J].Journal of Materials Science,2007(11):3856-3864. |
| [3] | Investigation on the activation of coal gangue by a new compound method[J].Journal of hazardous materials,2010(1/3):515. |
| [4] | Zhao M;Xiang Y .Natural rubber vulcanizate reinforced by modified coal-shale-based fillers[J].Journal of Applied Polymer Science,2004(3):1397-1400. |
| [5] | 宫晨琛,陶星,李东旭.煅烧煤矸石的活性和结构性能研究[J].材料导报,2005(02):115-117,120. |
| [6] | I. Lecomte;C. Henrist;M. Liegeois .(Micro)-structural comparison between geopolymers, alkali-activated slag cement and Portland cement[J].Journal of the European Ceramic Society,2006(16):3789-3797. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%