In order to improve the weldability of duplex stainless steels,obtaining more secondary austenite in the weld metal is an effective way.Therefore,optimizing the secondary austenite by changing its morphology,volume fraction and stability may be expected to enhance the ductility of the weld.The secondary austenite morphologies in the fusion zone of the laser continuously heat treated welds of 2205 duplex stainless steel were investigated.The secondary austenite morphologies were found to be influenced by different laser power level.The secondary austenite with penniform,freely grown and dendritic shape appeared in the course of 4,6 and 8 kW continuous heat treatment,respectively.It was found that there were three kinds of morphologies of secondary austenite in the fusion zone treated by different power,i.e.,widmannst¨atten austenite,grain boundary austenite and intragranular austenite.The results demonstrated that the mechanism of the secondary austenite formation was a displacement mechanism during the initial austenite lath formation and a diffusion mechanism during cooling.The nitrides provided the nitrogen for the transformation and at the same time acted as nucleation sites for the secondary austenite.
参考文献
| [1] | T.H. Chen;J.R. Yang .Microstructural characterization of simulated heat affected zone in a nitrogen-containing 2205 duplex stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):166-181. |
| [2] | J.-O.Nilsson;T.Huhtala .Structural stability of Super Duplex Stainless Weld Metals and Its Dependence on tungsten and copper[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1996(8):2196-2210. |
| [3] | T. Saeid;A. Abdollah-zadeh;H. Assadi;F. Malek Ghaini .Effect of friction stir welding speed on the microstructure and mechanical properties of a duplex stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):262-268. |
| [4] | H. C. WU;L W. TSAY;C. CHEN .Laser beam welding of 2205 Duplex Stainless Steel with metal Powder Additions[J].ISIJ International,2004(10):1720-1726. |
| [5] | E. Capello;P. Chiarello;B. Previtali .Laser welding and surface treatment of a 22Cr-5Ni-3Mo duplex stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):334-343. |
| [6] | Y. OHMORI;K. NAKAI;H. OHTSUBO .Mechanism of Widmanstatten austenite formation in a delta/gamma duplex phase stainless steel[J].ISIJ International,1995(8):969-975. |
| [7] | A. J. RAMIREZ;J. C. LIPPOLD;S. D. BRANDI .The Relationship between Chromium Nitride and Secondary Austenite Precipitation in Duplex Stainless Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2003(8):1575-1597. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%