采用X射线(XRD)、扫描电镜(SEM/EDAX)等手段,研究了一种镍基合金在850℃和950℃熔融NaCl的热腐蚀行为.结果表明:腐蚀期间,合金发生了高温氧化和热腐蚀行为;合金表面腐蚀产物分为3层,外层氧化物由Al2O3、AlTaO4和NiCr2O4组成,中间层氧化物为CrTaO4、NiWO4和WO3,而内层形成Al2O3内氧化物;且随腐蚀温度提高,合金表面的腐蚀层厚度及Al2O3内氧化层深度增加.
参考文献
| [1] | WANG Xin-yue;LI Xin;WANG Fu-hui et al.Influence of sputtered nanoerystalline coating on oxidation and hot corrosion of a nickel-based superalloy M951[J].Journal of Materials Science and Technology,2014,30(09):867-868. |
| [2] | Md Zatir Alama;Chatterjee D;Venkataraman B et al.Effect of cyclic oxidation on the tensile behavior of directionally solidified CM-247LC Ni-based superalloy at 870 ℃[J].Materials Science and Engineering A,2010,527:6211-6212. |
| [3] | 卢旭东,田素贵,王涛,朱德刚.溅射NiCrAlY纳米晶涂层在900℃的热腐蚀行为[J].材料热处理学报,2013(10):153-159. |
| [4] | ZHAO Shuang-qun;XIE Xi-shan;Gaylord D Smith .The oxidation behavior of the new nickel-based superalloy Inconel 740 with and without Na2SO4 deposit[J].Surface and Coatings Technology,2004,185:181-182. |
| [5] | 卢旭东,田素贵,于兴福,王常鑫.Ni-Cr-Ta-Al-Co-Mo合金在900℃和1000℃的恒温氧化行为[J].材料研究学报,2011(04):427-432. |
| [6] | Li YS;Spiegel M;Shimada S .Corrosion behaviour of various model alloys with NaCl-KCl coating[J].Materials Chemistry and Physics,2005(1):217-223. |
| [7] | MA Jun;JIANG Su-Meng;GONG Jun et al.Hot corrosion properties of composite coatings in the presence of NaCl at 700℃ and 900 ℃[J].Corrosion Science,2013,70:29-34. |
| [8] | Gosipathala C;Raja V S .Hot corrosion of YSZ/Al2O3 dispersed NiCrAlY plasma-sprayed coatings in Na2SO4-10wt.％ NaCl melt[J].Corrosion Science,2010,52:2600-2601. |
| [9] | Charng C T;Jams C R;Chaur J W et al.The hot corrosion of 310 stainless steel with pre-coated NaCl/Na2SO4 mixtures at 750℃[J].Materials Chemistry and Physics,2005,89:446-447. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%