采用CCT-AY-Ⅱ型钢板连续退火机模拟分析了退火时间对中锰TRIP钢0.1C-6Mn组织性能的影响规律.采用SEM、EBSD等微观方法观察不同工艺下制备的中锰TRIP的微观组织,利用XRD法测量了残留奥氏体量,实验测量了其力学性能.结果表明,650℃退火1 min时伸长率就达到了18％,抗拉强度1260 MPa,强塑积23 GPa％.通过EBSD证明试验钢退火马氏体只发生了回复,没有发生再结晶,且获得了超细晶组织.通过对保温3 min试验钢残留奥氏体研究,试验钢高的伸长率是由TRIP效应和组织的超细晶共同提供的.
参考文献
| [1] | 董瀚,王毛球,翁宇庆.高性能钢的M3组织调控理论与技术[J].钢铁,2010(07):1-7. |
| [2] | Han, HN;Oh, CS;Kim, G;Kwon, O .Design method for TRIP-aided multiphase steel based on a microstructure-based modelling for transformation-induced plasticity and mechanically induced martensitic transformation[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):462-468. |
| [3] | Frommeyer G;Brux U;Neumann P et al.Supra-ductile and high-strength manganese-TRIP/TWIP steels for high energy absorption purposes[J].ISIF International,2003,43:438-442. |
| [4] | Amar K. De;John G. Speer;David K. Matlock .COLOR TINT-ETCHING for Multiphase Steels[J].Advanced Materials & Processes,2003(2):27-30. |
| [5] | 李振,赵爱民,唐获,米振莉,焦殿辉.低碳中锰热轧TRIP钢退火工艺及组织演变[J].北京科技大学学报,2012(02):132-136. |
| [6] | 李楠,时捷,王存宇,赵晖,陈为亮,惠卫军,曹文全.两相区退火时间对冷轧中锰钢组织和力学性能的影响[J].材料热处理学报,2011(08):74-78. |
| [7] | 周玉.材料分析方法[M].北京:机械工业出版社,2006 |
| [8] | Lee S J;Lee S;Bruno C et al.Mn partitioning during the intercritical annealing of ultrafine-grained 6% Mn transformation-induced plasticity steel[J].Scripta Materialia,2011,64(07):649-652. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%