本文以乙烯基酯树脂和环氧树脂为基体,制备玻璃纤维增强树脂基复合材料拉-拉疲劳试件,研究应力振幅、铺层方式、树脂体系对树脂基复合材料疲劳性能的影响.结果表明,随着应力振幅的增加,GFRP试件的拉伸模量呈现单调下降；随着玻璃纤维布层数的增加,GFRP拉-拉疲劳性能会大幅下降；环氧树脂复合材料的疲劳性能要明显优于乙烯基酯树脂复合材料.
参考文献
| [1] | 沈观林;胡更开.复合材料力学[M].北京:清华大学出版社,2006 |
| [2] | 詹界东,杜修力,王作虎.HRP筋长期力学性能研究进展[J].玻璃钢/复合材料,2009(06):77-80. |
| [3] | 益小苏;杜善义;张立同.复合材料手册[M].北京:化学工业出版社,2009 |
| [4] | 刘泉,任宗栋,默增禄.复合材料在输电杆塔中的应用研究[J].玻璃钢/复合材料,2012(01):53-56. |
| [5] | Ulrich Hansen .Damage development in woven fabric composites during tension-tension fatigue[J].Journal of Composite Materials,1999(7):614-639. |
| [6] | Coats TW.;Harris CE. .EXPERIMENTAL VERIFICATION OF A PROGRESSIVE DAMAGE MODEL FOR IM7/5260 LAMINATES SUBJECTED TO TENSION-TENSION FATIGUE[J].Journal of Composite Materials,1995(3):280-305. |
| [7] | G. Caprino .Predicting fatigue life of composite laminates subjected to tension-tension fatigue[J].Journal of Composite Materials,2000(16):1334-1355. |
| [8] | E.K. Gamstedt;B.A. Sjogren .Micromechanisms in tension-compression fatigue of composite laminates containing transverse plies[J].Composites science and technology,1999(2):167-178. |
| [9] | Rotem A .The fatigue behaviour of orthotropic laminates under tension-compression loading[J].International Journal of Fatigue,1991,13(03):209-215. |
| [10] | 陈传尧.疲劳与断裂[M].武汉:华中科技大学出版社,2001 |
| [11] | 齐红宇,温卫东.先进纤维增强复合材料疲劳寿命的预测[J].玻璃钢复合材料,2000(05):6-9,13. |
| [12] | Hwang W;Han K S .Cumulative damage models and multistress fatigue life prediction[J].Journal of Composite Materials,1986,20:125-153. |
| [13] | Hwang W;Han K S .Fatigue of composites-Fatigue modulus concept and life prediction[J].Journal of Composite Materials,1986,20:154-165. |
| [14] | Ulrich Hansen .Damage development in woven fabric composites during tension-tension fatigue[J].Journal of Composite Materials,1999(7):614-639. |
| [15] | Khashaba UA .Fatigue and reliability analysis of unidirectional GFRP composites under rotating bending loads[J].Journal of Composite Materials,2003,37:317-330. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%